Deuterium diffusion in γ-LiAlO2 pellets irradiated with He+ and D2+ ions

Sequential irradiations of polycrystalline γ-LiAlO2 pellets were performed at 573 K with He+ and D2+ ions to overlap the deuterium (D) profile with the He+ ion damage peak. The D depth profiles were measured using time-of-flight secondary ion mass spectrometry before and after thermal annealing step...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Journal of nuclear materials 2020-09, Vol.538 (C), p.152357, Article 152357
Hauptverfasser:	Jiang, Weilin, Wang, Tianyao, Wang, Yining, Zhu, Zihua, Shao, Lin, Senor, David J.
Format:	Artikel
Sprache:	eng
Schlagworte:	Activation energy Annealing Concentration gradient Deuterium Deuterium diffusion Diffusion Diffusion coefficient Fluence Ion irradiation Ions Irradiation LiAlO2 Mass spectrometry Mass spectroscopy Neutron irradiation Pellets Secondary ion mass spectrometry Tritium Tritium breeder material
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!