A nonlocal peridynamics modeling approach for corrosion damage and crack propagation

[Display omitted] •Micro-chemically sensitive peridynamic modeling approach for corrosion damage.•Corrosion pits lead to incipient crack and growth under external loading.•Models pit nucleation, growth, coalescence, crack initiation and branching.•Crack propagation behavior is dependent on the exten...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Theoretical and applied fracture mechanics 2019-06, Vol.101 (C), p.373-387
Hauptverfasser:	Rokkam, Srujan, Gunzburger, Max, Brothers, Michael, Phan, Nam, Goel, Kishan
Format:	Artikel
Sprache:	eng
Schlagworte:	Computer simulation Continuum mechanics Corrosion Corrosion crack propagation Corrosion damage Corrosion effects Crack propagation Differential equations Finite element method Fracture mechanics Mathematical models Meshless methods Modeling Nonlocal model Nucleation Organic chemistry Peridynamics Pitting (corrosion) Propagation Repair & maintenance Stress corrosion cracking Structural damage
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!