Liquation behavior in the weld HAZ of high Si nodular iron

In the present study, liquation behavior including the constitutional liquation phenomena in the weld heataffected zone (HAZ) of nodular cast iron with 4% Si was investigated. The thermal cycle of the weld HAZ was simulated using a Gleeble simulator at various peak temperatures and a fast heating rate of 1000 °C/sec was selected to observe the constitutional liquation phenomenon. Differential thermal analysis has shown that the eutectic constituents of γ + Laves and γ + Fe 3 C begin to melt at 1120 °C and 1140 °C, respectively. Meanwhile, constitutional liquation by γ/graphite reaction occurred above 1140 °C, due to carbon enrichment around the graphite nodules.