[환경]촉매를 담지한 코디어라이트 필터의 VOC 제거 특성에 관한 연구

After porous filters were manufactured using cordierite powder whose mean particle size was 200 ${\mu}m$, they were loaded with catalysts such as Pt, Pd, Cu, Co, La, $V_2O_5$ by vacuum impregnation method. And we investigated the activity of catalysts used for catalytic oxidation of VOC by passing toluene through catalyst-loaded filters. The porous filters had the apparent porosity of 62%, the compressive strength of about 10 MPa and the pressure drop of 15 mmHg at the face velocity of 5 cm/sec. The loading of catalyst decreased the porosity of the filters and increased the pressure drop and the compressive strength of them. Among the catalysts, Pt had the highest activity for catalytic oxidation and could remove more than 90% of toluene at 250 $^{\circ}C$. Below 250 $^{\circ}C$, the content of Pt catalyst had an influence on the conversion of toluene but didn't show any influence above 250 $^{\circ}C$. 평균입경이 200 ${\mu}m$인 코디어라이트 분말로 다공성 필터를 제조한 후, 진공함침법으로 Pt, Pd, Cu, Co, La, $V_2O_5$ 촉매를 담지시켰다. VOC의 일종인 톨루엔을 촉매담지 세라믹필터에 통과시키며 촉매산화시킴으로서 톨루엔에 대한 촉매들의 활성에 대하여 고찰하였다. 제조된 다공성 필터의 겉보기 기공률은 62%였고, 압축강도는 약 10 MPa이었으며, 5 cm/sec 유속에서의 차압은 15 mmHg였다. 촉매를 필터에 담지시키면 기공률은 감소하고, 차압과 압축강도는 증가하였다. 필터에 담지된 촉매들 중에서 Pt 촉매의 활성이 가장 높았고, 250 $^{\circ}C$의 온도에서 90% 이상의 톨루엔을 제거시킬 수 있었다. 250 $^{\circ}C$ 이하의 온도에서는 Pt 촉매 담지량이 톨루엔의 전환율에 영향을 미쳤지만, 그 이상의 온도에서는 Pt 촉매 담지량의 차이에 의한 영향은 나타나지 않았다.