Crevice corrosion and environmentally assisted cracking of high-strength duplex stainless steels in simulated concrete pore solutions

•Study of high-strength duplex stainless steels and relevant corrosion mechanisms.•Mo content is influential on crevice corrosion resistance.•No stress corrosion cracking observed but hydrogen embrittlement can under overprotection. This paper presents a study of crevice corrosion and environmentall...

Ausführliche Beschreibung

Bibliographische Detailangaben

Veröffentlicht in:	Construction & building materials 2019-04, Vol.203, p.366-376
Hauptverfasser:	Moser, Robert D., Singh, Preet M., Kahn, Lawrence F., Kurtis, Kimberly E., Niño, David González, McClelland, Zackery B.
Format:	Artikel
Sprache:	eng
Schlagworte:	Analysis Carbonates Concrete Concrete cracking Concretes Corrosion (Chemistry) Crevice corrosion Cyclic voltammetry Electrochemical analysis Hydrogen embrittlement Mechanical properties Methods Stainless steel Steel corrosion Stress corrosion
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!