GAS-PERMEABLE POROUS BODY, ITS PRODUCTION AND PRESSURE CASTING MOLD

This invention relates to a gas-permeable porous body and production thereof by blending siliceous pagodite, limestone and clay in such a manner that SiO2? accounts for 70 to 88 wt.%, CaO 5 to 23 wt.% and Al2?O3? 5 to 15 wt.%, molding the mixture and sintering the mold at 1,000C or above. This porous body has an extremely uniform pore diameter and high gas-permeability and is used for a filter or an aeration member or for a mold for pressure casting. This invention relates also to a pressure casting mold having drain paths (5, 5') which are formed near the boundary surfaces between surface layers (50) and support layers (60). The surface layer (50) is made of the gas-permeable porous body described above. This mold makes it possible to release smoothly a thickened portion. Corps poreux perméable aux gaz et procédé de production de ce corps consistant à mélanger de la pagodite siliceuse, de la pierre à chaux et de l'argile de sorte que la teneur en SiO2 soit comprise entre 70 et 88 % en poids, la teneur en CaO entre 5 et 23 % en poids et la teneur en Al2O3 entre 5 er 15 % en poids, à mouler le mélange et à fritter le produit moulé à une température égale ou supérieure à 1000°C. Ce corps poreux présente des pores d'un diamètre extrêmement uniforme et une grande perméabilité aux gaz, et est utilisé dans un filtre ou un organe d'aération ou dans un moule de coulée sous pression. L'invention se rapporte également à un moule de coulée sous pression possédant des chemins de drain (5, 5') qui sont ménagés à proximité des surfaces frontière entre les couches de surface (50) et les couches de support (60). La couche de surface (50) se compose du corps poreux perméable aux gaz décrit ci-dessus. Ce moule permet le démoulage en douceur d'une pièce épaissie.