SILICON MATERIAL AND METHOD OF MANUFACTURE

A silicon material can include particles with a size between about 10 nanometers and 10 micrometers, where the particles can be porous or nonporous, and a coating disposed on the particles, wherein a thickness of the coating can be between about 1 nm and 1 µm. The coating can optionally include a carbon coating, graphite coating, or a polymeric coating. A method for coating a silicon material can include mixing the silicon material with a coating reagent, and heating the mixture of the silicon material and the coating reagent to a treatment temperature for a treatment time. The silicon material can optionally include primary particles that are clustered into secondary particles. The resulting coating can optionally include carbon coating, graphite coating, or a polymeric coating. Un matériau de silicium peut comprendre des particules ayant une taille comprise entre environ 10 nanomètres et 10 micromètres, les particules pouvant être poreuses ou non poreuses, et un revêtement disposé sur les particules, une épaisseur du revêtement pouvant être comprise entre environ 1 nm et 1 pm. Le revêtement peut éventuellement comprendre un revêtement de carbone, un revêtement de graphite ou un revêtement polymère. Un procédé de revêtement d'un matériau de silicium peut comprendre le mélange du matériau de silicium avec un réactif de revêtement, et le chauffage du mélange du matériau de silicium et du réactif de revêtement à une température de traitement pendant un temps de traitement. Le matériau de silicium peut éventuellement comprendre des particules primaires qui sont regroupées en particules secondaires. Le revêtement obtenu peut éventuellement comprendre un revêtement de carbone, un revêtement de graphite ou un revêtement polymère.