POLYPROPYLENE POLYETHYLENE MIXTURE UPGRADING

Use of a compatibilizer (B) for upgrading a polypropylene-polyethylene blend (A) comprising (A-1 ) polypropylene and (A-2) polyethylene wherein the weight ratio of polypropylene (A-1 ) to polyethylene (A-2) is in the range from 19:1 to 1:19 with respect to at least one or more of the following properties (i) elongation at break (ISO 527-1,2; F3/4), (ii) Charpy notched impact strength (1eA) (non-instrumented, ISO 179-1 at +23 °C), (iii) Charpy notched impact strength (1eA) (non-instrumented, ISO 179-1 at 0 °C), (iv) Charpy notched impact strength (1eA) (non-instrumented, ISO 179-1 at -20 °C), (v) puncture resistance (energy, IS07785-2 at +23°C) and (vi) low temperature puncture resistance (energy, ISO 7765-2 at 0°C or -20°C), wherein compatibilizer (B) is used in an amount of 1 to 35 wt.-% preferably 2 to 25 wt.-%, more preferably 3 to 9 wt.-% with respect to the final composition. Utilisation d'un agent de compatibilité (B) pour valoriser un mélange de polypropylène-polyéthylène (A) comprenant (A-1) du polypropylène et (A-2) du polyéthylène, le rapport en poids du polypropylène (A-1) au polyéthylène (A-2) étant compris entre 19:1 et 1:19 par rapport à au moins l'une des propriétés suivantes : (i) l'allongement à la rupture (ISO 527-1,2 ; F3/4), (ii) la résistance au choc Charpy d'éprouvettes entaillées (1eA) (non instrumentée, ISO 179-1 à +23 °C), (iii) la résistance au choc Charpy d'éprouvettes entaillées (1eA) (non instrumentée, ISO 179-1 à 0 °C), (iv) la résistance au choc Charpy d'éprouvettes entaillées (1eA) (non instrumentée, ISO 179-1 à -20 °C), (v) la résistance au percement (énergie, ISO 7785-2 à +23 °C) et (vi) la résistance au percement à basse température (énergie, ISO 7765-2 à 0 °C ou à -20 °C), l'agent de compatibilité (B) étant utilisé en une quantité comprise entre 1 et 35 % en poids, de préférence entre 2 et 25 % en poids, de préférence encore entre 3 et 9 % en poids par rapport à la composition finale.