ALUMINUM CASTING ALLOYS

An aluminum alloy comprising high amounts of manganese and/or strontium, and method of production of a cast part formed of the aluminum alloy in a direct chill counter pressure permanent mold casting system, is provided. In addition to the increased manganese and/or strontium, the aluminum alloy also contains silicon, iron, copper, magnesium, zinc, and aluminum. The casting system includes a mold defining a plurality of pores sized to allow quench media to enter the mold to cool the molten aluminum alloy contained therein without allowing the molten aluminum alloy to seep into the pores and out of the mold. The increased levels of manganese and/or strontium allows the molten aluminum alloy to be placed within the mold, solidified, and cleanly removed without having to add a releasing agent to the mold. L'invention concerne un alliage d'aluminium, comprenant des quantités élevées de manganèse et/ou de strontium, et un procédé de production d'une pièce coulée formée de l'alliage d'aluminium dans un système de coulage de moule permanent à contre-pression à refroidissement direct. Outre le manganèse et/ou le strontium accrus, l'alliage d'aluminium contient également du silicium, du fer, du cuivre, du magnésium, du zinc et de l'aluminium. Le système de coulage comporte un moule délimitant une pluralité de pores conçus pour permettre au milieu de trempe d'entrer dans le moule pour refroidir l'alliage d'aluminium fondu contenu dans ce dernier, sans permettre à l'alliage d'aluminium fondu de s'infiltrer dans les pores et hors du moule. Les taux accrus de manganèse et/ou de strontium permettent à l'alliage d'aluminium fondu d'être placé au sein du moule, solidifié et retiré de manière nette sans avoir à ajouter un agent de libération au moule.