COATED DENTAL ARTICLES AND RELATED METHODS OF MANUFACTURE

Provided are dental articles, and methods of making articles, having an aesthetic inorganic coating based on zirconia at least partially stabilized with yttrium oxide, calcium oxide, cerium oxide, or magnesium oxide. Stabilized zirconia coatings were found to provide a smooth, low friction surface having high abrasion resistance. These coatings are particularly applicable to orthodontic appliances. While virgin stabilized zirconia coatings can often have an undesirable color cast, it was discovered that this color cast can be substantially eliminated by heat treating the coated appliance in an oxygenated environment. The combination of depositing a stabilized zirconia coating and subsequently heat treating to decolorize the coating provides a surprisingly robust, stable, low-friction coating that is also aesthetic. La présente invention concerne des articles dentaires, et des procédés de fabrication des articles, comprenant un revêtement inorganique esthétique basé sur de la zircone stabilisée au moins en partie avec de l'oxyde d'yttrium, de l'oxyde de calcium, de l'oxyde de cérium, ou de l'oxyde de magnésium. Les revêtements à base de zircone stabilisée se sont avérés fournir une surface lisse à faible coefficient de friction ayant une résistance élevée à l'abrasion. Ces revêtements sont en particulier applicables à des appareils orthodontiques. Bien que des revêtements vierges à base de zircone stabilisée puissent souvent avoir une dominante de couleur indésirable, il s'est avéré que cette dominante de couleur peut être pratiquement éliminée par le biais d'un traitement à la chaleur de l'appareil enduit dans un environnement oxygéné. La combinaison du dépôt de revêtement de zircone stabilisée et par la suite du traitement à la chaleur pour décolorer le revêtement fournit un revêtement qui est de manière surprenante robuste, stable, à faible coefficient de friction mais également esthétique.