IONICALLY-CONDUCTIVE AMORPHOUS LITHIUM LANTHANUM ZIRCONIUM OXIDE

Amorphous lithium lanthanum zirconium oxide (LLZO) is formed as an ionically- conductive electrolyte medium. The LLZO comprises by percentage of total number of atoms from about 0.1% to about 50% lithium, from about 0.1% to about 25% lanthanum, from about 0.1% to about 25% zirconium, from about 30% to about 70%> oxygen and from 0.0% to about 25% carbon. At least one layer of amorphous LLZO may be formed through a sol-gel process wherein quantities of lanthanum methoxyethoxide, lithium butoxide and zirconium butoxide are dissolved in an alcohol-based solvent to form a mixture which is dispensed into a substantially planar configuration, transitioned through a gel phase, dried and cured to a substantially dry phase. L'invention concerne un oxyde de lithium, lanthane et zirconium (LLZO), amorphe, qui est formé en tant que milieu électrolyte conducteur d'ions. Le LLZO comporte, en pourcentage de nombre total d'atomes, d'environ 0,1 % à environ 50 % de lithium, d'environ 0,1 % à environ 25 % de lanthane, d'environ 0,1 % à environ 25 % de zirconium, d'environ 30 % à environ 70 %> d'oxygène et d'environ 0,0 % à environ 25 % de carbone. Au moins une couche de LLZO amorphe peut être formée par un procédé sol-gel, dans lequel des quantités de méthoxyéthylate de lanthane, de butylate de lithium et de butylate de zirconium sont dissoutes dans un solvant à base d'alcool pour former un mélange qui est distribué dans une configuration sensiblement plane, passe par une phase de gel, est séché et durci en une phase sensiblement sèche.