EXPANDABLE, INCOMBUSTIBLE POLYSTYRENE PARTICLES AND PREPARATION METHOD THEREOF, AND STYROPOR MADE FROM THE PARTICLES

The present invention relates to expandable, incombustible polystyrene particles and preparation method thereof, and styropor made from the particles. The method for preparing expandable polystyrene particles according to the present invention comprises the steps of: adding and agitating a 10~60 weight % of an incombustible powder substance with 1~70µm particle diameter to expandable polystyrene particles; softening the surface layer of the expandable polystyrene particles by spraying a mixture of water and solvent capable of dissolving polystyrene having 0.5~10weight % solvent thereby penetrating and coating the surface of the expandable polystyrene particles. Accordingly it is possible to mass produce incombustible styropor having excellent incombustibility, impact resistance, bending strength and an absorptance of 0.7(g/100cm2). La présente invention concerne des particules de polystyrène incombustible, expansible et un procédé de préparation associé, et du styropor fabriqué à partir des particules. Le procédé de préparation des particules de polystyrène expansible selon la présente invention comprend les étapes consistant à : ajouter et agiter de 10 à 60 % en poids d'une substance de poudre incombustible avec un diamètre de particules de 1 à 70 µm à des particules de polystyrène expansible ; ramollir la couche superficielle des particules de polystyrène expansible par pulvérisation d'un mélange d'eau et de solvant pouvant dissoudre le polystyrène ayant de 0,5 à 10 % en poids de solvant pénétrant et enduisant ainsi la surface des particules de polystyrène expansible. Par conséquent, il est possible de produire en masse du styropor incombustible doté d'une excellente incombustibilité, d'une résistance aux chocs, d'une résistance à la flexion et d'un facteur d'absorption de 0,7 (g/100cm2).