MIXTURE FOR PRODUCTION OF POLYCRYSTALLINE HEXAFERRITE

FIELD: electronics. SUBSTANCE: invention relates to composition of mixture for production of strontium hexaferrite. Proposed mixture includes oxide compound of iron with proportion of FeO: FeO=1:(0.43-0.47) and strontium carbonate which is mixed chemically with 1.5-2.5 per cent be mass of lanthanum (in terms of oxide). Strontium hexaferrite with residual induction Br= 3920-4100 Gs, coercive force H=2100-2450 Oe and magnetic energy BH= 3.52-3.78 MGs.Oe is produced with use of proposed mixture. Process of production of hexaferrite is simplified due to improvement of technological characteristics of mixture. EFFECT: increased magnetic characteristics of hexaferrite and simplified technology of its production. 1 tbl Изобретение относится к составу шихты для получения гексаферрита стронция и может быть использовано в электронной промышленности. Цель изобретения - повышение магнитных характеристик гексаферрита и упрощение технологии получения. Предложенная шихта содержит оксидное соединение железа при отношении FeO:FeO = 1:(0,43-0,47) и карбонат стронция с химически замещенным на 1,5 - 2,5 мас.% лантаном (в пересчете на оксид). С использованием предложенной шихты получен гексаферрит стронция с остаточной индукцией Br = 3920 - 4100 Гс, коэрцитивной силой H= 2100 - 2450 Э и магнитной энергией BH= 3,52-3,78 МГс·Э . Технология получения гексаферрита упрощается за счет улучшения технологических характеристик шихты. 1 табл.