METHOD AND APPARATUS FOR SIMULTANEOUSLY COMPACTING AND CAKING CONDUCTING POWDERS

FIELD: powder metallurgy. SUBSTANCE: prior to be caked, powder is compacted under pressure up to 25 MPa in absence of current and then, when pressure is reduced to 5-10 MPa, pulse alternating sinusoidal current with frequency 45-65 Hz and density 3.2-6.8 A/sq.mm is passed for 10-80 s and then, with density increased to 10.6-15.4 A/sq.mm, for further 5-110 s. Apparatus involved has punches that are simultaneously current supply pathways, refractory material casing reinforced with in-tension band. Between punches and powder being caked, division interlayer composed of graphite powder (60-85 vol.%) and alumina (15-40 vol.%) is available. EFFECT: reduced electric and mechanical power of equipment. 1. Способ одновременного уплотнения и спекания электропроводящих порошков, включающий непосредственное пропускание импульсного тока через находящийся под давлением порошок, отличающийся тем, что перед спеканием порошок уплотняют давлением до 25 МПа без тока, а затем, уменьшив давление до 5-10 МПа, пропускают знакопеременный синусоидный ток частотой 45-65 Гц различной плотности: сначала плотностью 3,2-6,8 А/ммв течение 10-80 с, потом плотностью 10,6-15,4 А/ммв течение 5-110 с.2. Устройство для одновременного уплотнения и спекания электропроводящих порошков, состоящее из корпуса, двух пуансонов, двух токоподводов, двух прокладок между пуансоном и порошком, отличающееся тем, что корпус выполнен из огнеупорного материала, например из оксида бериллия или оксида циркония, и укреплен стальным бандажом внатяг, пуансоны одновременно являются токоподводами, а в качестве прокладок использована смесь порошков графита и оксида алюминия при следующем соотношении компонентов, об.%:Графит - 60-85Оксид алюминия - 15-40