NICKEL-BASED HEAT-RESISTANT CAST ALLOY AND ARTICLE MADE THEREFROM

FIELD: metallurgy.SUBSTANCE: invention relates to metallurgy, in particular, to corrosion-resistant heat-resistant nickel-based alloys for parts of hot-path of gas turbine engines and plants operating in aggressive media at temperatures of 800-1,000 °C. Nickel-based heat-resistant foundry alloy contains, wt%: carbon 0.10-0.20, chromium 21.5-23.5, cobalt 18.0-20.0, titanium 3.0-4.5, tungsten 1.0-3.0, aluminum 1.0-3.0, tantalum 0.8-2.5, zirconium up to 0.15, boron up to 0.020, niobium 0.5-1.5, lanthanum up to 0.20, barium up to 0.10, nickel making the rest.EFFECT: alloy is characterized by high values of long-term strength, sulphide-oxide and chloride corrosion resistance, as well as manufacturability and structural stability at temperature of 850 °C.3 cl, 2 tbl, 7 ex Изобретение относится к металлургии, в частности к коррозионно-стойким жаропрочным сплавам на основе никеля для деталей горячего тракта газотурбинных двигателей и установок, длительно работающих в агрессивных средах при температурах 800-1000°С. Жаропрочный литейный сплав на основе никеля содержит, мас.%: углерод 0,10-0,20, хром 21,5-23,5, кобальт 18,0-20,0, титан 3,0-4,5, вольфрам 1,0-3,0, алюминий 1,0-3,0, тантал 0,8-2,5, цирконий до 0,15, бор до 0,020, ниобий 0,5-1,5, лантан до 0,20, барий до 0,10, никель - остальное. Сплав характеризуется высокими значениями длительной прочности, сульфидно-оксидной и хлоридной коррозионной стойкости, а также технологичностью и структурной стабильностью при температуре 850°С. 2 н. и 1 з.п. ф-лы, 2 табл., 7 пр.