THICK SHEET OF STRUCTURAL STEEL FOR MANUFACTURING DETAILS OF WELDED STRUCTURES AND METHOD FOR ITS PRODUCTION IN NORMALIZED CONDITION
FIELD: metallurgy.SUBSTANCE: steel sheet thickness up to 50 mm contains, wt %: C 0.10-0.14, Si 0.16-0.30, Mn 1.35-1.60, Al 0.02-0.05, S not more than 0.005, P not more than 0.018, Ti 0.010 -0.025, Nb 0.025-0.040, V+Nb+Ti not more than 0.07, Cr+Ni+Cu not more than 0.3, N not more than 0.007, Fe and i...
Gespeichert in:
Hauptverfasser: | , , , , , |
---|---|
Format: | Patent |
Sprache: | eng ; rus |
Schlagworte: | |
Online-Zugang: | Volltext bestellen |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
container_end_page | |
---|---|
container_issue | |
container_start_page | |
container_title | |
container_volume | |
creator | Vaurin Vitalij Vasilevich Smelov Anton Igorevich Sychev Oleg Nikolaevich Mikheev Vyacheslav Viktorovich Korchagin Andrej Mikhajlovich Sakharov Maksim Sergeevich |
description | FIELD: metallurgy.SUBSTANCE: steel sheet thickness up to 50 mm contains, wt %: C 0.10-0.14, Si 0.16-0.30, Mn 1.35-1.60, Al 0.02-0.05, S not more than 0.005, P not more than 0.018, Ti 0.010 -0.025, Nb 0.025-0.040, V+Nb+Ti not more than 0.07, Cr+Ni+Cu not more than 0.3, N not more than 0.007, Fe and impurities the rest. At that Seq≤0.43% has ferrite and perlite microstructure, yield strength is at least 335 MPa, temporary resistance is at least 470 MPa, elongation is at least 22%, KV impact work at minus 50°C at least 34 J. When the sheet is produced, the continuously poured blank is heated to 1190-1210°C, conduct rough rolling at a starting temperature not lower than 950°C thickness of at least two thicknesses of the finished sheet, with relative reduction per pass of at least 10% for not less than 80% of the number of crimps in roughing, finishing rolling at a starting temperature based on Tst=(-1.05×h+860)±10°C, where h is the thickness of the sheet, mm, 1.05 is the empirical coefficient determined experimentally, °C/mm, and completed at a temperature of 820±10°C, after which the sheet is cooled in air.EFFECT: ensuring weldability and increased impact performance at low temperatures.2 cl, 3 tbl
Изобретение относится к области металлургии. Для обеспечения свариваемости и повышенной работы удара при низких температурах стальной лист толщиной до 50 мм содержит, мас. %: C 0,10-0,14, Si 0,16-0,30, Mn 1,35-1,60, Al 0,02-0,05, S не более 0,005, P не более 0,018, Ti 0,010-0,025, Nb 0,025-0,040, V+ Nb+ Ti не более 0,07, Cr+Ni+ Cu не более 0,3, N не более 0,007, Fe и примеси остальное, причем Сэкв ≤ 0,43%, имеет микроструктуру феррита и перлита, предел текучести по меньшей мере 335 МПа, временное сопротивление по меньшей мере 470 МПа, относительное удлинение по меньшей мере 22%, работа удара KV при минус 50°С по меньшей мере 34 Дж. При получении листа непрерывнолитую заготовку нагревают до 1190-1210°С, проводят черновую прокатку при температуре начала не ниже 950°Се на толщину, составляющую не менее двух толщин готового листа, с относительными обжатиями за проход не менее 10% для не менее чем 80% от количества обжатий при черновой прокатке, чистовую прокатку при температуре начала исходя из Тнчп=(-1,05×h+860)±10°С, где h - толщина листа, мм, 1,05 - эмпирический коэффициент, определенный опытным путем, °С/мм, и завершают при температуре 820±10°С, после чего лист охлаждают на воздухе. 2 н.п. ф-лы, 3 табл. |
format | Patent |
fullrecord | <record><control><sourceid>epo_EVB</sourceid><recordid>TN_cdi_epo_espacenet_RU2630721C1</recordid><sourceformat>XML</sourceformat><sourcesystem>PC</sourcesystem><sourcerecordid>RU2630721C1</sourcerecordid><originalsourceid>FETCH-epo_espacenet_RU2630721C13</originalsourceid><addsrcrecordid>eNqNi0EKwjAQRbtxIeod5gKCbUHXIZmYwTSRZILgphSJK9FCPYIHtxVx7ep__n9vXrzYkDxANIgMXkPkkCSnIOxYES1oH6ARLmkxzeT2oJAF2TjRJ7QK1U_CCMIpaJCNVx-TOMIxeDXe5B2QA-dDIyydR016p2jal8Xs2t2GvPrmogCNLM069482D313yff8bEOqtvVmV5WyrP9A3hfYPVA</addsrcrecordid><sourcetype>Open Access Repository</sourcetype><iscdi>true</iscdi><recordtype>patent</recordtype></control><display><type>patent</type><title>THICK SHEET OF STRUCTURAL STEEL FOR MANUFACTURING DETAILS OF WELDED STRUCTURES AND METHOD FOR ITS PRODUCTION IN NORMALIZED CONDITION</title><source>esp@cenet</source><creator>Vaurin Vitalij Vasilevich ; Smelov Anton Igorevich ; Sychev Oleg Nikolaevich ; Mikheev Vyacheslav Viktorovich ; Korchagin Andrej Mikhajlovich ; Sakharov Maksim Sergeevich</creator><creatorcontrib>Vaurin Vitalij Vasilevich ; Smelov Anton Igorevich ; Sychev Oleg Nikolaevich ; Mikheev Vyacheslav Viktorovich ; Korchagin Andrej Mikhajlovich ; Sakharov Maksim Sergeevich</creatorcontrib><description>FIELD: metallurgy.SUBSTANCE: steel sheet thickness up to 50 mm contains, wt %: C 0.10-0.14, Si 0.16-0.30, Mn 1.35-1.60, Al 0.02-0.05, S not more than 0.005, P not more than 0.018, Ti 0.010 -0.025, Nb 0.025-0.040, V+Nb+Ti not more than 0.07, Cr+Ni+Cu not more than 0.3, N not more than 0.007, Fe and impurities the rest. At that Seq≤0.43% has ferrite and perlite microstructure, yield strength is at least 335 MPa, temporary resistance is at least 470 MPa, elongation is at least 22%, KV impact work at minus 50°C at least 34 J. When the sheet is produced, the continuously poured blank is heated to 1190-1210°C, conduct rough rolling at a starting temperature not lower than 950°C thickness of at least two thicknesses of the finished sheet, with relative reduction per pass of at least 10% for not less than 80% of the number of crimps in roughing, finishing rolling at a starting temperature based on Tst=(-1.05×h+860)±10°C, where h is the thickness of the sheet, mm, 1.05 is the empirical coefficient determined experimentally, °C/mm, and completed at a temperature of 820±10°C, after which the sheet is cooled in air.EFFECT: ensuring weldability and increased impact performance at low temperatures.2 cl, 3 tbl
Изобретение относится к области металлургии. Для обеспечения свариваемости и повышенной работы удара при низких температурах стальной лист толщиной до 50 мм содержит, мас. %: C 0,10-0,14, Si 0,16-0,30, Mn 1,35-1,60, Al 0,02-0,05, S не более 0,005, P не более 0,018, Ti 0,010-0,025, Nb 0,025-0,040, V+ Nb+ Ti не более 0,07, Cr+Ni+ Cu не более 0,3, N не более 0,007, Fe и примеси остальное, причем Сэкв ≤ 0,43%, имеет микроструктуру феррита и перлита, предел текучести по меньшей мере 335 МПа, временное сопротивление по меньшей мере 470 МПа, относительное удлинение по меньшей мере 22%, работа удара KV при минус 50°С по меньшей мере 34 Дж. При получении листа непрерывнолитую заготовку нагревают до 1190-1210°С, проводят черновую прокатку при температуре начала не ниже 950°Се на толщину, составляющую не менее двух толщин готового листа, с относительными обжатиями за проход не менее 10% для не менее чем 80% от количества обжатий при черновой прокатке, чистовую прокатку при температуре начала исходя из Тнчп=(-1,05×h+860)±10°С, где h - толщина листа, мм, 1,05 - эмпирический коэффициент, определенный опытным путем, °С/мм, и завершают при температуре 820±10°С, после чего лист охлаждают на воздухе. 2 н.п. ф-лы, 3 табл.</description><language>eng ; rus</language><subject>ALLOYS ; CHEMISTRY ; FERROUS OR NON-FERROUS ALLOYS ; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUSMETALS OR ALLOYS ; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHERTREATMENTS ; MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVINGMATERIAL ; METALLURGY ; METALLURGY OF IRON ; MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS ; PERFORMING OPERATIONS ; PUNCHING METAL ; ROLLING OF METAL ; TRANSPORTING ; TREATMENT OF ALLOYS OR NON-FERROUS METALS</subject><creationdate>2017</creationdate><oa>free_for_read</oa><woscitedreferencessubscribed>false</woscitedreferencessubscribed></display><links><openurl>$$Topenurl_article</openurl><openurlfulltext>$$Topenurlfull_article</openurlfulltext><thumbnail>$$Tsyndetics_thumb_exl</thumbnail><linktohtml>$$Uhttps://worldwide.espacenet.com/publicationDetails/biblio?FT=D&date=20170912&DB=EPODOC&CC=RU&NR=2630721C1$$EHTML$$P50$$Gepo$$Hfree_for_read</linktohtml><link.rule.ids>230,308,780,885,25564,76547</link.rule.ids><linktorsrc>$$Uhttps://worldwide.espacenet.com/publicationDetails/biblio?FT=D&date=20170912&DB=EPODOC&CC=RU&NR=2630721C1$$EView_record_in_European_Patent_Office$$FView_record_in_$$GEuropean_Patent_Office$$Hfree_for_read</linktorsrc></links><search><creatorcontrib>Vaurin Vitalij Vasilevich</creatorcontrib><creatorcontrib>Smelov Anton Igorevich</creatorcontrib><creatorcontrib>Sychev Oleg Nikolaevich</creatorcontrib><creatorcontrib>Mikheev Vyacheslav Viktorovich</creatorcontrib><creatorcontrib>Korchagin Andrej Mikhajlovich</creatorcontrib><creatorcontrib>Sakharov Maksim Sergeevich</creatorcontrib><title>THICK SHEET OF STRUCTURAL STEEL FOR MANUFACTURING DETAILS OF WELDED STRUCTURES AND METHOD FOR ITS PRODUCTION IN NORMALIZED CONDITION</title><description>FIELD: metallurgy.SUBSTANCE: steel sheet thickness up to 50 mm contains, wt %: C 0.10-0.14, Si 0.16-0.30, Mn 1.35-1.60, Al 0.02-0.05, S not more than 0.005, P not more than 0.018, Ti 0.010 -0.025, Nb 0.025-0.040, V+Nb+Ti not more than 0.07, Cr+Ni+Cu not more than 0.3, N not more than 0.007, Fe and impurities the rest. At that Seq≤0.43% has ferrite and perlite microstructure, yield strength is at least 335 MPa, temporary resistance is at least 470 MPa, elongation is at least 22%, KV impact work at minus 50°C at least 34 J. When the sheet is produced, the continuously poured blank is heated to 1190-1210°C, conduct rough rolling at a starting temperature not lower than 950°C thickness of at least two thicknesses of the finished sheet, with relative reduction per pass of at least 10% for not less than 80% of the number of crimps in roughing, finishing rolling at a starting temperature based on Tst=(-1.05×h+860)±10°C, where h is the thickness of the sheet, mm, 1.05 is the empirical coefficient determined experimentally, °C/mm, and completed at a temperature of 820±10°C, after which the sheet is cooled in air.EFFECT: ensuring weldability and increased impact performance at low temperatures.2 cl, 3 tbl
Изобретение относится к области металлургии. Для обеспечения свариваемости и повышенной работы удара при низких температурах стальной лист толщиной до 50 мм содержит, мас. %: C 0,10-0,14, Si 0,16-0,30, Mn 1,35-1,60, Al 0,02-0,05, S не более 0,005, P не более 0,018, Ti 0,010-0,025, Nb 0,025-0,040, V+ Nb+ Ti не более 0,07, Cr+Ni+ Cu не более 0,3, N не более 0,007, Fe и примеси остальное, причем Сэкв ≤ 0,43%, имеет микроструктуру феррита и перлита, предел текучести по меньшей мере 335 МПа, временное сопротивление по меньшей мере 470 МПа, относительное удлинение по меньшей мере 22%, работа удара KV при минус 50°С по меньшей мере 34 Дж. При получении листа непрерывнолитую заготовку нагревают до 1190-1210°С, проводят черновую прокатку при температуре начала не ниже 950°Се на толщину, составляющую не менее двух толщин готового листа, с относительными обжатиями за проход не менее 10% для не менее чем 80% от количества обжатий при черновой прокатке, чистовую прокатку при температуре начала исходя из Тнчп=(-1,05×h+860)±10°С, где h - толщина листа, мм, 1,05 - эмпирический коэффициент, определенный опытным путем, °С/мм, и завершают при температуре 820±10°С, после чего лист охлаждают на воздухе. 2 н.п. ф-лы, 3 табл.</description><subject>ALLOYS</subject><subject>CHEMISTRY</subject><subject>FERROUS OR NON-FERROUS ALLOYS</subject><subject>GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUSMETALS OR ALLOYS</subject><subject>MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHERTREATMENTS</subject><subject>MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVINGMATERIAL</subject><subject>METALLURGY</subject><subject>METALLURGY OF IRON</subject><subject>MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS</subject><subject>PERFORMING OPERATIONS</subject><subject>PUNCHING METAL</subject><subject>ROLLING OF METAL</subject><subject>TRANSPORTING</subject><subject>TREATMENT OF ALLOYS OR NON-FERROUS METALS</subject><fulltext>true</fulltext><rsrctype>patent</rsrctype><creationdate>2017</creationdate><recordtype>patent</recordtype><sourceid>EVB</sourceid><recordid>eNqNi0EKwjAQRbtxIeod5gKCbUHXIZmYwTSRZILgphSJK9FCPYIHtxVx7ep__n9vXrzYkDxANIgMXkPkkCSnIOxYES1oH6ARLmkxzeT2oJAF2TjRJ7QK1U_CCMIpaJCNVx-TOMIxeDXe5B2QA-dDIyydR016p2jal8Xs2t2GvPrmogCNLM069482D313yff8bEOqtvVmV5WyrP9A3hfYPVA</recordid><startdate>20170912</startdate><enddate>20170912</enddate><creator>Vaurin Vitalij Vasilevich</creator><creator>Smelov Anton Igorevich</creator><creator>Sychev Oleg Nikolaevich</creator><creator>Mikheev Vyacheslav Viktorovich</creator><creator>Korchagin Andrej Mikhajlovich</creator><creator>Sakharov Maksim Sergeevich</creator><scope>EVB</scope></search><sort><creationdate>20170912</creationdate><title>THICK SHEET OF STRUCTURAL STEEL FOR MANUFACTURING DETAILS OF WELDED STRUCTURES AND METHOD FOR ITS PRODUCTION IN NORMALIZED CONDITION</title><author>Vaurin Vitalij Vasilevich ; Smelov Anton Igorevich ; Sychev Oleg Nikolaevich ; Mikheev Vyacheslav Viktorovich ; Korchagin Andrej Mikhajlovich ; Sakharov Maksim Sergeevich</author></sort><facets><frbrtype>5</frbrtype><frbrgroupid>cdi_FETCH-epo_espacenet_RU2630721C13</frbrgroupid><rsrctype>patents</rsrctype><prefilter>patents</prefilter><language>eng ; rus</language><creationdate>2017</creationdate><topic>ALLOYS</topic><topic>CHEMISTRY</topic><topic>FERROUS OR NON-FERROUS ALLOYS</topic><topic>GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUSMETALS OR ALLOYS</topic><topic>MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHERTREATMENTS</topic><topic>MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVINGMATERIAL</topic><topic>METALLURGY</topic><topic>METALLURGY OF IRON</topic><topic>MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS</topic><topic>PERFORMING OPERATIONS</topic><topic>PUNCHING METAL</topic><topic>ROLLING OF METAL</topic><topic>TRANSPORTING</topic><topic>TREATMENT OF ALLOYS OR NON-FERROUS METALS</topic><toplevel>online_resources</toplevel><creatorcontrib>Vaurin Vitalij Vasilevich</creatorcontrib><creatorcontrib>Smelov Anton Igorevich</creatorcontrib><creatorcontrib>Sychev Oleg Nikolaevich</creatorcontrib><creatorcontrib>Mikheev Vyacheslav Viktorovich</creatorcontrib><creatorcontrib>Korchagin Andrej Mikhajlovich</creatorcontrib><creatorcontrib>Sakharov Maksim Sergeevich</creatorcontrib><collection>esp@cenet</collection></facets><delivery><delcategory>Remote Search Resource</delcategory><fulltext>fulltext_linktorsrc</fulltext></delivery><addata><au>Vaurin Vitalij Vasilevich</au><au>Smelov Anton Igorevich</au><au>Sychev Oleg Nikolaevich</au><au>Mikheev Vyacheslav Viktorovich</au><au>Korchagin Andrej Mikhajlovich</au><au>Sakharov Maksim Sergeevich</au><format>patent</format><genre>patent</genre><ristype>GEN</ristype><title>THICK SHEET OF STRUCTURAL STEEL FOR MANUFACTURING DETAILS OF WELDED STRUCTURES AND METHOD FOR ITS PRODUCTION IN NORMALIZED CONDITION</title><date>2017-09-12</date><risdate>2017</risdate><abstract>FIELD: metallurgy.SUBSTANCE: steel sheet thickness up to 50 mm contains, wt %: C 0.10-0.14, Si 0.16-0.30, Mn 1.35-1.60, Al 0.02-0.05, S not more than 0.005, P not more than 0.018, Ti 0.010 -0.025, Nb 0.025-0.040, V+Nb+Ti not more than 0.07, Cr+Ni+Cu not more than 0.3, N not more than 0.007, Fe and impurities the rest. At that Seq≤0.43% has ferrite and perlite microstructure, yield strength is at least 335 MPa, temporary resistance is at least 470 MPa, elongation is at least 22%, KV impact work at minus 50°C at least 34 J. When the sheet is produced, the continuously poured blank is heated to 1190-1210°C, conduct rough rolling at a starting temperature not lower than 950°C thickness of at least two thicknesses of the finished sheet, with relative reduction per pass of at least 10% for not less than 80% of the number of crimps in roughing, finishing rolling at a starting temperature based on Tst=(-1.05×h+860)±10°C, where h is the thickness of the sheet, mm, 1.05 is the empirical coefficient determined experimentally, °C/mm, and completed at a temperature of 820±10°C, after which the sheet is cooled in air.EFFECT: ensuring weldability and increased impact performance at low temperatures.2 cl, 3 tbl
Изобретение относится к области металлургии. Для обеспечения свариваемости и повышенной работы удара при низких температурах стальной лист толщиной до 50 мм содержит, мас. %: C 0,10-0,14, Si 0,16-0,30, Mn 1,35-1,60, Al 0,02-0,05, S не более 0,005, P не более 0,018, Ti 0,010-0,025, Nb 0,025-0,040, V+ Nb+ Ti не более 0,07, Cr+Ni+ Cu не более 0,3, N не более 0,007, Fe и примеси остальное, причем Сэкв ≤ 0,43%, имеет микроструктуру феррита и перлита, предел текучести по меньшей мере 335 МПа, временное сопротивление по меньшей мере 470 МПа, относительное удлинение по меньшей мере 22%, работа удара KV при минус 50°С по меньшей мере 34 Дж. При получении листа непрерывнолитую заготовку нагревают до 1190-1210°С, проводят черновую прокатку при температуре начала не ниже 950°Се на толщину, составляющую не менее двух толщин готового листа, с относительными обжатиями за проход не менее 10% для не менее чем 80% от количества обжатий при черновой прокатке, чистовую прокатку при температуре начала исходя из Тнчп=(-1,05×h+860)±10°С, где h - толщина листа, мм, 1,05 - эмпирический коэффициент, определенный опытным путем, °С/мм, и завершают при температуре 820±10°С, после чего лист охлаждают на воздухе. 2 н.п. ф-лы, 3 табл.</abstract><oa>free_for_read</oa></addata></record> |
fulltext | fulltext_linktorsrc |
identifier | |
ispartof | |
issn | |
language | eng ; rus |
recordid | cdi_epo_espacenet_RU2630721C1 |
source | esp@cenet |
subjects | ALLOYS CHEMISTRY FERROUS OR NON-FERROUS ALLOYS GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUSMETALS OR ALLOYS MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHERTREATMENTS MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVINGMATERIAL METALLURGY METALLURGY OF IRON MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS PERFORMING OPERATIONS PUNCHING METAL ROLLING OF METAL TRANSPORTING TREATMENT OF ALLOYS OR NON-FERROUS METALS |
title | THICK SHEET OF STRUCTURAL STEEL FOR MANUFACTURING DETAILS OF WELDED STRUCTURES AND METHOD FOR ITS PRODUCTION IN NORMALIZED CONDITION |
url | https://sfx.bib-bvb.de/sfx_tum?ctx_ver=Z39.88-2004&ctx_enc=info:ofi/enc:UTF-8&ctx_tim=2024-12-28T18%3A35%3A49IST&url_ver=Z39.88-2004&url_ctx_fmt=infofi/fmt:kev:mtx:ctx&rfr_id=info:sid/primo.exlibrisgroup.com:primo3-Article-epo_EVB&rft_val_fmt=info:ofi/fmt:kev:mtx:patent&rft.genre=patent&rft.au=Vaurin%20Vitalij%20Vasilevich&rft.date=2017-09-12&rft_id=info:doi/&rft_dat=%3Cepo_EVB%3ERU2630721C1%3C/epo_EVB%3E%3Curl%3E%3C/url%3E&disable_directlink=true&sfx.directlink=off&sfx.report_link=0&rft_id=info:oai/&rft_id=info:pmid/&rfr_iscdi=true |