METHOD FOR DEHYDROGENISATION OF WELDS OF PIPELINES

FIELD: gas industry.SUBSTANCE: invention relates to analysis of materials with radiation methods and can be used for de-hydrogenisation of welds of pipelines. When making a weld joint, its temperature is measured and when one of points of said joint reaches temperature of 200-240 °C output of electronic accelerator is placed above. Accelerator is turned on and joint is irradiated with electrons, while controlling temperature of weld joint. When temperature of joint drops to 60-80 °C, accelerator is moved along joint to other points thereof radially across surface of welded pipes, repeating process of measuring temperature and irradiation of joint with electrons.EFFECT: invention enables to dehydrogenise weld joints of main gas pipelines during manufacturing process due to electron irradiation which in turn enables to eliminate embrittlement of pipeline joints and increases service life.1 cl, 3 dwg, 1 ex Изобретение относится к анализу материалов радиационными методами и может быть использовано для разводороживания сварных швов магистральных газопроводов. При изготовлении сварного шва измеряют его температуру и при достижении в одной из точек шва температуры 200-240ºС над ней устанавливают выпускное устройство ускорителя электронов. Включают ускоритель и облучают шов электронами, одновременно контролируя температуру сварного шва. При снижении температуры шва до 60-80ºС перемещают ускоритель вдоль шва к другим его точкам радиально по поверхности свариваемых труб, повторяя процесс измерения температуры и облучения шва электронами. Изобретение позволяет разводороживать сварные швы магистральных газопроводов в процессе их изготовления за счет облучения электронами, что, в свою очередь, обеспечивает возможность устранения охрупчивания швов газопровода и увеличивает срок его службы. 3 ил., 1 пр.