METHOD OF FERROVANADIUM MANUFACTURING

FIELD: metallurgy.SUBSTANCE: under this method prior to the charge mixer loading on the furnace hearth the mixture of periclase powder and boric acid in ratio 1:(0.01-0.05) and in quantity 0.06-0.30 of weight of the melted alloy is supplied. The restoration period of melting is performed at aluminium content in liquid semi-finished product 5-15%, and ratio of vanadium pentoxide to lime in the charge mixture at the beginning of the restoration period is 1:(0.15-0.30), then during refining period - 1:(0.31-0.40). The refining mixture additionally contains aluminium in amount of 0.02-0.10 of weight of vanadium pentoxide.EFFECT: invention increases vanadium extraction, reduces aluminium and firebricks consumption, increases productivity and improves quality.2 tbl Изобретение относится к области металлургии, в частности к производству ферросплавов. В способе перед загрузкой шихтовой смеси на подину печи задают смесь периклазового порошка и борной кислоты, взятых в соотношении 1:(0,01-0,05) и в количестве 0,06-0,30 от массы выплавляемого сплава, при этом восстановительный период плавки проводят при содержании алюминия в жидком полупродукте 5-15%, а соотношение пентоксида ванадия и извести в шихтовой смеси вначале на восстановительном периоде плавки составляет 1:(0,15-0,30), затем на рафинировочном периоде 1:(0,31-0,40), при этом рафинировочная смесь дополнительно содержит алюминий в количестве 0,02-0,10 от массы пентоксида ванадия. Изобретение позволяет повысить извлечение ванадия на 0,5-1,6%, снизить расход алюминия на 0,6-1,7% и огнеупоров на 15-20%, увеличить производительность на 13-20% и улучшить качество сплава. 2 табл.