METHOD OF OBTAINING CATALYST OF AFTERBURNING PROPANE ON GLASSFIBRE CARRIER

FIELD: chemistry.SUBSTANCE: catalyst is obtained by impregnation of glass fibre carrier (structured in form of material, woven from threads with 1 mm diameter) with film-generating solution, maturation of which is realised at temperature 20-22°C for 4-5 days, and its further step-by-step thermal processing - at 60°C for 30-40 minutes and at 700°C for 1 hour, with the following ratio of initial solution components, wt %: titanium tetra-n-butoxide from 4.09 to 4.13, tetraethoxysilane from 0 to 1.49, cobalt(II) chloride tetrahydrate from 2.15 to 3.41, hydrochloric acid 0.27, distilled water from 0.56 to 1.04, n-butyl alcohol - the remaining part.EFFECT: increased level of purification.1 tbl, 2 dwg, 3 ex Изобретение относится к области каталитической химии и может быть использовано при очистке промышленных газовых выбросов и выбросов автотранспорта от углеводородов. Катализатор получают пропиткой стекловолокнистого носителя (структурированного в виде материала, тканого из нитей диаметром 1 мм) пленкообразующим раствором, созревание которого осуществляется при температуре 20-22°С в течение 4-5 суток, и его последующей ступенчатой термической обработкой - при 60°С в течение 30-40 минут и при 700°С в течение 1 часа, при следующем соотношении компонентов исходного раствора, мас.%: тетра-н-бутоксид титана от 4,09 до 4,13, тетраэтоксисилан от 0 до 1,49, гексагидрат хлорида кобальта(II) от 2,15 до 3,41, соляная кислота 0,27, дистиллированная вода от 0,56 до 1,04, н-бутиловый спирт остальное. 1 табл., 2 ил., 3 пр.