METAL OF WELD JOINT FOR BONDING PARENT METALS FROM COPPER-NICKEL ALLOYS WITH NICKEL CONTENT OF 9,0-41,0 WT

FIELD: metallurgy. ^ SUBSTANCE: invention relates to metallurgy and may be used in production and repair of ship outboard pipelines, fish protection devices and other structures. Proposed weld joint metal comprises the following components, in wt %: nickel - 10.0-42.0, iron - 0.70-1.70, manganese - 0.50-1.20, silicon - 0.07-0.30, titanium - 0.05-0.30, copper making the rest. For every weld joint, nickel content in weld joint material should exceed that in parent metal by 1.0-10.0%. ^ EFFECT: more positive stationary potential in sea water of weld joint compared to that of parent metal, rules out defects. ^ 1 tbl Изобретение относится к области металлургии, а именно к металлам сварных швов для соединения между собой медно-никелевых сплавов с содержанием от 9,0 до 41,0 мас.% никеля, и может быть использовано при изготовлении и ремонте судовых трубопроводов систем забортной воды кораблей и судов всех типов и назначений, рыбозащитных устройств и других конструкций и изделий из рассматриваемых медно-никелевых сплавов. Металл сварного шва для соединения основных металлов из медно-никелевых сплавов с содержанием 9,0-41,0 мас.% никеля содержит компоненты, мас.%: никель - 10,0-42,0, железо - 0,70-1,70, марганец - 0,50-1,20, кремний - 0,07-0,30, титан - 0,05-0,30, медь - остальное. Для каждого сварного соединения содержание никеля в металле шва должно быть больше, чем его содержание в основном металле, на 1,0-10,0 мас.%. Металл шва имеет более положительный стационарный потенциал в морской воде, чем стационарный потенциал в морской воде основного металла, а также в нем отсутствуют такие недопустимые дефекты, как трещины, плены, повышенная пористость. 1 табл.