ANNEALING METHOD IN BELL FURNACE

FIELD: metallurgy. ^ SUBSTANCE: piles of rolls with temperature of 190-210C are subjected at speed of 25-80C/h to annealing beginning temperature of 610-670C, exposure for 7-36 hours is performed at temperature decrease to annealing end temperature of 580-640C; at that, annealing beginning temperature is higher than annealing end temperature by 20-40C; then, at temperature of not more than 550C there performed is accelerated cooling under muffle with its blowing with cold protective gas; unpacking is performed at temperature of not more than 120C with further cooling in the air; after the annealing exposure is completed and heating is switched off, cooling under heating cap is carried out for not more than 13 hours. ^ EFFECT: reducing power consumption and obtaining the required set of mechanical properties with increased strength class of 260 to 420 heating. ^ 2 cl, 1 ex, 2 tbl Изобретение относится к области черной металлургии, конкретно к технологии отжига в колпаковой печи рулонных холоднокатаных полос из низкоуглеродистой стали, предназначенных для изготовления деталей автомобиля методом штамповки. Для снижения расхода энергоресурсов и получения требуемого комплекса механических свойств с повышенным классом прочности от 260 до 420 нагрев стопы рулонов от 190-210°С ведут со скоростью 25-80°С/ч до температуры начала отжига 610-670°С, производят выдержку продолжительностью 7-36 часов при понижении температуры до температуры конца отжига 580-640°С, при этом температура начала отжига на 20-40°С выше температуры конца отжига, затем с температуры не более 550°С осуществляют ускоренное охлаждение под муфелем с продувкой его холодным защитным газом, распаковку производят при температуре не более 120°С с последующим охлаждением на воздухе, истечении выдержки при отжиге и отключении нагрева производят охлаждение под нагревательным колпаком не более 13 часов. 1 з.п. ф-лы, 2 табл.,1 пр.