AUSTENITE CORROSION-RESISTANT STEEL AND ITEM MANUFACTURED OF IT

FIELD: metallurgy. ^ SUBSTANCE: steel contains carbon, silicon, manganese, chromium, nickel, nitrogen, zirconium, iron and unavoidable impurities at following ratio of components, wt %: carbon ëñ 0.03, manganese 0.07 - 2.0, silicon 2.2 - 4.5, chromium 14.0 - 16.0, nickel 8.5 - 11.5, nitrogen 0.1 - 0.25, zirconium 0.05 - 0.12, iron and unavoidable impurities the rest. Contents of chromium, silicon, nickel and nitrogen are determined by dependence (Cr+0.75Si)/(2.2Ni+40N)=0.550.8, while contents of carbon, nitrogen and zirconium are determined with dependence (30C+50N)/18Zr=49. ^ EFFECT: raised resistance to general and inter-crystal corrosion in boiling nitric acid of various concentration; fabrication of qualitative welded connections at maintained level of strength and processability; increased efficiency of composition. ^ 5 cl, 3 tbl Изобретение относится к области металлургии, а именно к составам коррозионно-стойких аустенитных сталей, предназначенных для производства листовых и трубных деталей, сварных конструкций, контактирующих с кипящей азотной кислотой. Сталь содержит углерод, кремний, марганец, хром, никель, азот, цирконий, железо и неизбежные примеси при следующем соотношении компонентов, мас.%: углерод ≤0,03, марганец 0,07-2,0, кремний 2,2-4,5, хром 14,0-16,0, никель 8,5-11,5, азот 0,1-0,25, цирконий 0,05-0,12, железо и неизбежные примеси остальное. Содержания хрома, кремния, никеля и азота связаны зависимостью (Cr+0,75Si)/(2,2Ni+40N)=0,55÷0,8, а содержания углерода, азота и циркония связаны зависимостью (30С+50N)/18Zr=4÷9. Повышается стойкость против общей и межкристаллитной коррозии в кипящей азотной кислоте различной концентрации, обеспечивается возможность получения качественных сварных соединений при сохранении уровня прочности и технологичности, а также повышается экономичность композиции. 2 н. и 3 з.п. ф-лы, 4 табл.