METHOD OF PRODUCING OXIDE HEXAGONAL FERRIMAGNET POWDER WITH W-STRUCTURE

FIELD: process engineering. ^ SUBSTANCE: invention relates to method of producing ferrite powders to be used in radio electronics as radio radiation absorbing coatings. Initial BaO2, Fe2O3, CoO, ZnO and Fe powders are dried and mechanically mixed. Produced mix is thermally treated by combustion. Then mechanical activation is performed at energy-intensivity factor of 40 to 60 g for 10 to 40 min and sintered at 1230-1250C for 60-240 min. Produced material comprises 96 to 98 vol. % of W-phase and features increased magnetic characteristics and uniform magnetic properties. ^ EFFECT: increased uniformity of composition and magnetic properties of hexagonal ferrimagnet. ^ 1 tbl Изобретение относится к способам получения ферритовых порошков для применения в радиотехнике и радиоэлектронике в качестве радиопоглощающих покрытий. Исходные порошки BaO2, Fe2O3, СоО, ZnO, Fe сушат и осуществляют смешение простым перемешиванием. Полученную смесь термообрабатывают в режиме технологического горения, после чего проводят механическую активацию при факторе энергонапряженности, равном 40-60 g, в течение 10-40 минут и осуществляют последующее спекание при температуре 1230-1250°С в течение 60-240 минут. Полученный материал содержит 96-98 об.% W-фазы и имеет более высокие магнитные характеристики и однородность магнитных свойств. Обеспечивается повышение однородности состава и магнитных свойств гексагонального ферримагнетика. 1 табл.