PROCESS FOR PREPARING REFRACTORY TRANSITION METALS BY ELECTROCHEMICAL REDUCTION

The invention relates to a process for preparing hard-fusible transition metals such as Ti, Zr, V, Mn, Fe, Ni, Co, Mo, W, Cr, Ta, Nb, Cu and the like. According to the invention, the process comprises a process of electrochemical reduction of the above-mentioned metal oxides in molten calcium chloride as electrolyte, in argon-protected atmosphere, using one of the metal oxides in the shape of a sintered-pressed disk as solid cathode and a superdense graphite as anode, so that the working temperature ranges between 800...900°C, the applied voltage is from 2.5 to 3.2 V, the current intensity is from 10 to 20 A, the initial cathode density is from 3.2 to 4.5 A/cm, the distance between the anode and the cathode is from 20 to 40 mm, the anode/cathode surface ratio is from 1.5...2/1. Invenţia se referă la un procedeu de obţinere a unor metale de tranziţie, greu fuzibile, ca, de exemplu, Ti, Zr, V, Mn, Fe, Ni, Co, Mo, W, Cr, Si, Ta, Nb, Cu şi altele asemenea. Procedeul conform invenţiei constă într-un proces de reducere electrochimică a oxizilor metalelor mai sus menţionate, în baie de electrolit de clorură de calciu topită, în atmosferă protejată de argon, utilizând drept catod solid unul dintre oxizii metalici sub formă de disc presat - sinterizat şi un anod de grafit superdens, astfel încât, pentru obţinerea fiecărui metal cu conţinuturi reduse de oxigen şi de impurităţi, temperatura de lucru este cuprinsă între 800...900°C, tensiunea aplicată este de 2,5...3,2 V, intensitatea curentului electric este de 10...20 A, densitatea catodică de curent iniţială este de 3,2...4,5 A/cm, distanţa între anod şi catod este cuprinsă între 20...40 mm, iar raportul suprafeţelor anod/catod este cuprins între 1,5...2/1.