1 Room-Temperature Curable One Liquid Type Composite Resin Coating Material And Manufacturing Method Thereof

According to exemplary embodiments of the present invention, a room temperature curing one-liquid type composite resin coating agent may be prepared by removing 22.7 wt% or more of methanol by fractional distillation from 100 wt% of a composite resin composition prepared by mixing and reacting three different types of alkoxysilanes, water, IBA, TBAC, and other substances at a ratio of 54.51 to 56.83: 7.21 to 7.97: 6.07 to 6.58: 27.95 to 28.97: 1.77 to 2.15. The three different types of alkoxysilanes may be GPTMS, MTMS, and DMDMS, respectively, and the input ratio of MTMS may be higher than the sum of the input ratios of GPTMS and DMDMS. The room temperature curing one-liquid type composite resin coating agent may be composed of 40 to 50% solid content and 50 to 60% liquid content and may be cured by making a reaction with moisture in the air at room temperature. In addition, the room temperature curing one-liquid type composite resin coating agent may have high adhesive strength and therefore may be applied to fields in which the use of an inorganic resin was previously difficult. 본 발명의 예시적인 실시예들에 따른 상온경화형 1액형 복합수지 코팅제는, 서로 다른 세 종류의 알콕시실란, 물, IBA, TBAC, 및 기타 물질이, 54.51 내지 56.83 : 7.21 내지 7.97 : 6.07 내지 6.58 : 27.95 내지 28.97 : 1.77 내지 2.15 의 비율로 혼합 및 반응하여 제조된 복합수지 조성물 100 중량%로부터, 22.7 중량% 이상의 메탄올을 분별증류로 제거함으로써 제조될 수 있다. 상기 서로 다른 세 종류의 알콕시실란은 각각 GPTMS, MTMS 및 DMDMS일 수 있으며, MTMS의 투입 비율은 GPTMS와 DMDMS의 투입 비율 합보다 높을 수 있다. 상기 상온경화형 1액형 복합수지 코팅제는 40% 내지 50%의 고형분과, 50% 내지 60%의 액상분으로 이루어질 수 있으며, 상온에서 공기 중의 습기와 반응하여 경화될 수 있다.