TILE MATERIAL

To realize "improvement of construction efficiency" and the like by providing the release sheet with a protrusion protruding from the edge of the tile body or by setting the coefficient of thermal expansion of the release sheet lower than that of the tile body.SOLUTION: A tile material 1 has an adhesive layer 3 laminated on one surface 2a of a tile body 2. The tile material has a release sheet 4 covering the adhesive layer 3. The release sheet 4 is provided with a protrusion 5 protruding from the tile body 2 in a plan view. The release coefficient of thermal expansion B4 is lower than the tile coefficient of thermal expansion B2 in at least one direction. The release peeling adhesive strength H4 is 0.8 times or less of the tile peeling adhesive strength H2 and 0.01 N/25 mm or more. Also, the tile body 2 may not contain glass fiber. In the tile body 2, a clear layer 6, a print layer 7 and a base layer 8 may be laminated in this order. The adhesive layer 3 may be laminated on the side of the base layer 8 containing vinyl chloride resin. A release coat layer 10 may be laminated on the other surface 9b of a synthetic resin film 9 in the release sheet 4.SELECTED DRAWING: Figure 1 【課題】離型シートにタイル本体の端縁からはみ出る突出部を設けたり、離型シートの熱膨張率をタイル本体の熱膨張率より低くすること等により、「施工効率の向上」などを実現する。【解決手段】タイル本体２の一方面２ａに粘着層３が積層されたタイル材１である。粘着層３を覆う離型シート４を有し、離型シート４に平面視でタイル本体２からはみ出た突出部５を設けたり、少なくとも一方向で離型熱膨張率Ｂ４はタイル熱膨張率Ｂ２より低かったり、離型剥離接着強さＨ４はタイル剥離接着強さＨ２の０．８倍以下で且つ０．０１Ｎ／２５ｍｍ以上である。又、タイル本体２はガラス繊維を含んでいなかったり、タイル本体２は、クリア層６、プリント層７及びベース層８がこの順に積層され、塩化ビニル樹脂を含んだベース層８側に前記粘着層３が積層されていたり、離型シート４における合成樹脂フィルム９の他方面９ｂ等に離型コート層１０が積層されていても良い。【選択図】図１