Inspecting rolled prods. for surface defects - where prods. are coated with indicator soln. and subjected to high frequency induction heating which reveals the defects

The surface of the rolled prod. is coated with a substance (A) forming a background for a second substance (B) which changes colour when heated. High frequency heating is then used so that defects on or near the surface of the prod. cause a thermochemical change in substance (B) altering its colour so the defects are clearly visible. When substance (B) is used as a soln., drying is pref. used for coating (B) at a temp. below that causing its colour to change. Substances (A,B) may alternatively be combined in an aq. colloidal suspension, contg. 30-160 g/l KOH in soln. and 5-20 g/l soluble potato starch. Used for inspection of ingots and slabs which still have a scaled surface due to hot rolling, or for examining profiles, e.g. rails or girders. The invention can be used without prior surface treatment of the rolled prods. L'invention concerne le contrôle non destructif des matériaux. Le procédé faisant l'objet de l'invention est du type comprenant l'application sur le produit 1 d'un revêtement indicateur contenant une substance de fond et une substance de contraste, et est caractérisé notamment en ce que la substance de contraste utilisée est une substance thermosensible changeant de couleur à une température déterminée, et en ce que le revêtement indicateur est appliqué sur le produit 1 à une température relativement basse, puis le produit est chauffé par induction à haute fréquence jusqu'à une température suffisante pour créer le gradient de température nécessaire à la transformation thermochimique de la substance de contraste et son changement de couleur aux endroits où le produit présente des défauts. L'invention peut être utilisée en particulier pour le contrôle de la qualité de la surface des demi-produits laminés à chaud, sans decalaminage de leur surface.