WASSERDAMPFDURCHLÄSSIGES UND WASSERUNDURCHLÄSSIGES VERBUNDGEWEBE, DIESES ENTHALTENDER WASSERUNDURCHLÄSSIGER GEGENSTAND SOWIE VERFAHREN ZUR HERSTELLUNG DESSELBEN

A water-vapor-permeable waterproof composite fabric having high flexibility, water pressure resistance and water laundering resistance is constituted from a substrate fabric and a polyether-ester elastomer (PEE-A) film layer laminated to the substrate fabric through a polyether-ester elastomer (PEE-...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
1. Verfasser:	HONNA, HIROSHI
Format:	Patent
Sprache:	ger
Schlagworte:	ACCESSORIES AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F,C08G CHEMISTRY COMPOSITIONS BASED THEREON FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR FLEXIBLE SHEET MATERIAL NOT OTHERWISE PROVIDED FOR GENERAL PROCESSES OF COMPOUNDING HUMAN NECESSITIES LAUNDERING LAYERED PRODUCTS LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT ORNON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM METALLURGY ORGANIC MACROMOLECULAR COMPOUNDS OUTERWEAR PERFORMING OPERATIONS PROTECTIVE GARMENTS TEXTILES THEIR PREPARATION OR CHEMICAL WORKING-UP TRANSPORTING TREATMENT OF TEXTILES OR THE LIKE WALL, FLOOR OR LIKE COVERING MATERIALS, e.g. LINOLEUM,OILCLOTH, ARTIFICIAL LEATHER, ROOFING FELT, CONSISTING OF AFIBROUS WEB COATED WITH A LAYER OF MACROMOLECULARMATERIAL WEARING APPAREL WORKING-UP
Online-Zugang:	Volltext bestellen
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Beschreibung
Zusammenfassung:	A water-vapor-permeable waterproof composite fabric having high flexibility, water pressure resistance and water laundering resistance is constituted from a substrate fabric and a polyether-ester elastomer (PEE-A) film layer laminated to the substrate fabric through a polyether-ester elastomer (PEE-B) binder layer, each of PEE-A and PEE-B including polyalkylene glycol residues, alkyleneglycol residues and dicarboxylic acid residues, in which composite fabric, (1) the PEE-A contains 5 to 25 % by mass of polyethyleneglycol residues, (2) the PEE-A film layer is 5 to 5 mu thick, (3) the PEE-B has a melting temperature of at least 20 DEG C below that of the PEE-A and (4) the PEE-B binder layer is present in an amount of 2 to 20 g/m .