690MPa-grade steel plate with excellent low-temperature ductility and manufacturing method
The invention provides a 690 MPa grade steel plate with excellent low-temperature ductility and a manufacturing method. The steel plate comprises the following components in percentage by weight: 0.100%-0.180% of C, 0.15%-0.75% of Si, 0.80%-1.60% of Mn, 0.060%-0.200% of V, 0.40%-0.80% of Cu, 2.50%-3...
Gespeichert in:
| Hauptverfasser: | , , , , , , , , , |
|---|---|
| Format: | Patent |
| Sprache: | chi ; eng |
| Schlagworte: | |
| Online-Zugang: | Volltext bestellen |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| container_end_page | |
|---|---|
| container_issue | |
| container_start_page | |
| container_title | |
| container_volume | |
| creator | QI XIANGYU WANG HUA WANG XIAOHANG CHEN HUA ZHANG PENG LI GUANGLONG LI BOYONG HAN PENG YAN LING YING CHUANTAO |
| description | The invention provides a 690 MPa grade steel plate with excellent low-temperature ductility and a manufacturing method. The steel plate comprises the following components in percentage by weight: 0.100%-0.180% of C, 0.15%-0.75% of Si, 0.80%-1.60% of Mn, 0.060%-0.200% of V, 0.40%-0.80% of Cu, 2.50%-3.50% of Ni, 0.80%-1.80% of Cr, 0.60%-1.60% of Mo, 0.020%-0.070% of La, 0.0020%-0.0040% of B, less than or equal to 0.008% of P, less than or equal to 0.003% of S and the balance of Fe and inevitable impurities. The manufacturing method comprises the steps of smelting, continuous casting, casting blank cooling, heating in a heating furnace, rolling, cooling and tempering. The tensile properties of the steel plate at-40 DEG C are as follows: the yield strength is 750MPa or above, the tensile strength is 840MPa or above, and the percentage elongation after fracture is 23.0% or above. The impact energy of the steel plate at-80 DEG C is greater than 200J, the ductile-brittle transition temperature FATT is less than-75 D |
| format | Patent |
| fullrecord | <record><control><sourceid>epo_EVB</sourceid><recordid>TN_cdi_epo_espacenet_CN116875903A</recordid><sourceformat>XML</sourceformat><sourcesystem>PC</sourcesystem><sourcerecordid>CN116875903A</sourcerecordid><originalsourceid>FETCH-epo_espacenet_CN116875903A3</originalsourceid><addsrcrecordid>eNqNyjEOgkAQRmEaC6PeYTwACYSIUhqisdFYWNmQye4PbDIsGxiC3l4LD2D1iu8to2deJNc7x83AFjQqIBSEFTQ7bQkvAxF4JennWNEFDKzTALKTUSdO38TeUsd-qtl8xfmGOmjb23W0qFlGbH5dRdvz6VFeYoS-whjYwEOr8pam-WG_K5LsmP3zfAD5qzsh</addsrcrecordid><sourcetype>Open Access Repository</sourcetype><iscdi>true</iscdi><recordtype>patent</recordtype></control><display><type>patent</type><title>690MPa-grade steel plate with excellent low-temperature ductility and manufacturing method</title><source>esp@cenet</source><creator>QI XIANGYU ; WANG HUA ; WANG XIAOHANG ; CHEN HUA ; ZHANG PENG ; LI GUANGLONG ; LI BOYONG ; HAN PENG ; YAN LING ; YING CHUANTAO</creator><creatorcontrib>QI XIANGYU ; WANG HUA ; WANG XIAOHANG ; CHEN HUA ; ZHANG PENG ; LI GUANGLONG ; LI BOYONG ; HAN PENG ; YAN LING ; YING CHUANTAO</creatorcontrib><description>The invention provides a 690 MPa grade steel plate with excellent low-temperature ductility and a manufacturing method. The steel plate comprises the following components in percentage by weight: 0.100%-0.180% of C, 0.15%-0.75% of Si, 0.80%-1.60% of Mn, 0.060%-0.200% of V, 0.40%-0.80% of Cu, 2.50%-3.50% of Ni, 0.80%-1.80% of Cr, 0.60%-1.60% of Mo, 0.020%-0.070% of La, 0.0020%-0.0040% of B, less than or equal to 0.008% of P, less than or equal to 0.003% of S and the balance of Fe and inevitable impurities. The manufacturing method comprises the steps of smelting, continuous casting, casting blank cooling, heating in a heating furnace, rolling, cooling and tempering. The tensile properties of the steel plate at-40 DEG C are as follows: the yield strength is 750MPa or above, the tensile strength is 840MPa or above, and the percentage elongation after fracture is 23.0% or above. The impact energy of the steel plate at-80 DEG C is greater than 200J, the ductile-brittle transition temperature FATT is less than-75 D</description><language>chi ; eng</language><subject>ALLOYS ; CASTING ; CASTING OF METALS ; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES ; CHEMISTRY ; FERROUS OR NON-FERROUS ALLOYS ; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUSMETALS OR ALLOYS ; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHERTREATMENTS ; METALLURGY ; METALLURGY OF IRON ; MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS ; PERFORMING OPERATIONS ; POWDER METALLURGY ; PROCESSING OF PIG-IRON, e.g. REFINING, MANUFACTURE OFWROUGHT-IRON OR STEEL ; TRANSPORTING ; TREATMENT IN MOLTEN STATE OF FERROUS ALLOYS ; TREATMENT OF ALLOYS OR NON-FERROUS METALS</subject><creationdate>2023</creationdate><oa>free_for_read</oa><woscitedreferencessubscribed>false</woscitedreferencessubscribed></display><links><openurl>$$Topenurl_article</openurl><openurlfulltext>$$Topenurlfull_article</openurlfulltext><thumbnail>$$Tsyndetics_thumb_exl</thumbnail><linktohtml>$$Uhttps://worldwide.espacenet.com/publicationDetails/biblio?FT=D&date=20231013&DB=EPODOC&CC=CN&NR=116875903A$$EHTML$$P50$$Gepo$$Hfree_for_read</linktohtml><link.rule.ids>230,308,776,881,25542,76289</link.rule.ids><linktorsrc>$$Uhttps://worldwide.espacenet.com/publicationDetails/biblio?FT=D&date=20231013&DB=EPODOC&CC=CN&NR=116875903A$$EView_record_in_European_Patent_Office$$FView_record_in_$$GEuropean_Patent_Office$$Hfree_for_read</linktorsrc></links><search><creatorcontrib>QI XIANGYU</creatorcontrib><creatorcontrib>WANG HUA</creatorcontrib><creatorcontrib>WANG XIAOHANG</creatorcontrib><creatorcontrib>CHEN HUA</creatorcontrib><creatorcontrib>ZHANG PENG</creatorcontrib><creatorcontrib>LI GUANGLONG</creatorcontrib><creatorcontrib>LI BOYONG</creatorcontrib><creatorcontrib>HAN PENG</creatorcontrib><creatorcontrib>YAN LING</creatorcontrib><creatorcontrib>YING CHUANTAO</creatorcontrib><title>690MPa-grade steel plate with excellent low-temperature ductility and manufacturing method</title><description>The invention provides a 690 MPa grade steel plate with excellent low-temperature ductility and a manufacturing method. The steel plate comprises the following components in percentage by weight: 0.100%-0.180% of C, 0.15%-0.75% of Si, 0.80%-1.60% of Mn, 0.060%-0.200% of V, 0.40%-0.80% of Cu, 2.50%-3.50% of Ni, 0.80%-1.80% of Cr, 0.60%-1.60% of Mo, 0.020%-0.070% of La, 0.0020%-0.0040% of B, less than or equal to 0.008% of P, less than or equal to 0.003% of S and the balance of Fe and inevitable impurities. The manufacturing method comprises the steps of smelting, continuous casting, casting blank cooling, heating in a heating furnace, rolling, cooling and tempering. The tensile properties of the steel plate at-40 DEG C are as follows: the yield strength is 750MPa or above, the tensile strength is 840MPa or above, and the percentage elongation after fracture is 23.0% or above. The impact energy of the steel plate at-80 DEG C is greater than 200J, the ductile-brittle transition temperature FATT is less than-75 D</description><subject>ALLOYS</subject><subject>CASTING</subject><subject>CASTING OF METALS</subject><subject>CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES</subject><subject>CHEMISTRY</subject><subject>FERROUS OR NON-FERROUS ALLOYS</subject><subject>GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUSMETALS OR ALLOYS</subject><subject>MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHERTREATMENTS</subject><subject>METALLURGY</subject><subject>METALLURGY OF IRON</subject><subject>MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS</subject><subject>PERFORMING OPERATIONS</subject><subject>POWDER METALLURGY</subject><subject>PROCESSING OF PIG-IRON, e.g. REFINING, MANUFACTURE OFWROUGHT-IRON OR STEEL</subject><subject>TRANSPORTING</subject><subject>TREATMENT IN MOLTEN STATE OF FERROUS ALLOYS</subject><subject>TREATMENT OF ALLOYS OR NON-FERROUS METALS</subject><fulltext>true</fulltext><rsrctype>patent</rsrctype><creationdate>2023</creationdate><recordtype>patent</recordtype><sourceid>EVB</sourceid><recordid>eNqNyjEOgkAQRmEaC6PeYTwACYSIUhqisdFYWNmQye4PbDIsGxiC3l4LD2D1iu8to2deJNc7x83AFjQqIBSEFTQ7bQkvAxF4JennWNEFDKzTALKTUSdO38TeUsd-qtl8xfmGOmjb23W0qFlGbH5dRdvz6VFeYoS-whjYwEOr8pam-WG_K5LsmP3zfAD5qzsh</recordid><startdate>20231013</startdate><enddate>20231013</enddate><creator>QI XIANGYU</creator><creator>WANG HUA</creator><creator>WANG XIAOHANG</creator><creator>CHEN HUA</creator><creator>ZHANG PENG</creator><creator>LI GUANGLONG</creator><creator>LI BOYONG</creator><creator>HAN PENG</creator><creator>YAN LING</creator><creator>YING CHUANTAO</creator><scope>EVB</scope></search><sort><creationdate>20231013</creationdate><title>690MPa-grade steel plate with excellent low-temperature ductility and manufacturing method</title><author>QI XIANGYU ; WANG HUA ; WANG XIAOHANG ; CHEN HUA ; ZHANG PENG ; LI GUANGLONG ; LI BOYONG ; HAN PENG ; YAN LING ; YING CHUANTAO</author></sort><facets><frbrtype>5</frbrtype><frbrgroupid>cdi_FETCH-epo_espacenet_CN116875903A3</frbrgroupid><rsrctype>patents</rsrctype><prefilter>patents</prefilter><language>chi ; eng</language><creationdate>2023</creationdate><topic>ALLOYS</topic><topic>CASTING</topic><topic>CASTING OF METALS</topic><topic>CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES</topic><topic>CHEMISTRY</topic><topic>FERROUS OR NON-FERROUS ALLOYS</topic><topic>GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUSMETALS OR ALLOYS</topic><topic>MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHERTREATMENTS</topic><topic>METALLURGY</topic><topic>METALLURGY OF IRON</topic><topic>MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS</topic><topic>PERFORMING OPERATIONS</topic><topic>POWDER METALLURGY</topic><topic>PROCESSING OF PIG-IRON, e.g. REFINING, MANUFACTURE OFWROUGHT-IRON OR STEEL</topic><topic>TRANSPORTING</topic><topic>TREATMENT IN MOLTEN STATE OF FERROUS ALLOYS</topic><topic>TREATMENT OF ALLOYS OR NON-FERROUS METALS</topic><toplevel>online_resources</toplevel><creatorcontrib>QI XIANGYU</creatorcontrib><creatorcontrib>WANG HUA</creatorcontrib><creatorcontrib>WANG XIAOHANG</creatorcontrib><creatorcontrib>CHEN HUA</creatorcontrib><creatorcontrib>ZHANG PENG</creatorcontrib><creatorcontrib>LI GUANGLONG</creatorcontrib><creatorcontrib>LI BOYONG</creatorcontrib><creatorcontrib>HAN PENG</creatorcontrib><creatorcontrib>YAN LING</creatorcontrib><creatorcontrib>YING CHUANTAO</creatorcontrib><collection>esp@cenet</collection></facets><delivery><delcategory>Remote Search Resource</delcategory><fulltext>fulltext_linktorsrc</fulltext></delivery><addata><au>QI XIANGYU</au><au>WANG HUA</au><au>WANG XIAOHANG</au><au>CHEN HUA</au><au>ZHANG PENG</au><au>LI GUANGLONG</au><au>LI BOYONG</au><au>HAN PENG</au><au>YAN LING</au><au>YING CHUANTAO</au><format>patent</format><genre>patent</genre><ristype>GEN</ristype><title>690MPa-grade steel plate with excellent low-temperature ductility and manufacturing method</title><date>2023-10-13</date><risdate>2023</risdate><abstract>The invention provides a 690 MPa grade steel plate with excellent low-temperature ductility and a manufacturing method. The steel plate comprises the following components in percentage by weight: 0.100%-0.180% of C, 0.15%-0.75% of Si, 0.80%-1.60% of Mn, 0.060%-0.200% of V, 0.40%-0.80% of Cu, 2.50%-3.50% of Ni, 0.80%-1.80% of Cr, 0.60%-1.60% of Mo, 0.020%-0.070% of La, 0.0020%-0.0040% of B, less than or equal to 0.008% of P, less than or equal to 0.003% of S and the balance of Fe and inevitable impurities. The manufacturing method comprises the steps of smelting, continuous casting, casting blank cooling, heating in a heating furnace, rolling, cooling and tempering. The tensile properties of the steel plate at-40 DEG C are as follows: the yield strength is 750MPa or above, the tensile strength is 840MPa or above, and the percentage elongation after fracture is 23.0% or above. The impact energy of the steel plate at-80 DEG C is greater than 200J, the ductile-brittle transition temperature FATT is less than-75 D</abstract><oa>free_for_read</oa></addata></record> |
| fulltext | fulltext_linktorsrc |
| identifier | |
| ispartof | |
| issn | |
| language | chi ; eng |
| recordid | cdi_epo_espacenet_CN116875903A |
| source | esp@cenet |
| subjects | ALLOYS CASTING CASTING OF METALS CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES CHEMISTRY FERROUS OR NON-FERROUS ALLOYS GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUSMETALS OR ALLOYS MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHERTREATMENTS METALLURGY METALLURGY OF IRON MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS PERFORMING OPERATIONS POWDER METALLURGY PROCESSING OF PIG-IRON, e.g. REFINING, MANUFACTURE OFWROUGHT-IRON OR STEEL TRANSPORTING TREATMENT IN MOLTEN STATE OF FERROUS ALLOYS TREATMENT OF ALLOYS OR NON-FERROUS METALS |
| title | 690MPa-grade steel plate with excellent low-temperature ductility and manufacturing method |
| url | https://sfx.bib-bvb.de/sfx_tum?ctx_ver=Z39.88-2004&ctx_enc=info:ofi/enc:UTF-8&ctx_tim=2025-02-11T23%3A20%3A30IST&url_ver=Z39.88-2004&url_ctx_fmt=infofi/fmt:kev:mtx:ctx&rfr_id=info:sid/primo.exlibrisgroup.com:primo3-Article-epo_EVB&rft_val_fmt=info:ofi/fmt:kev:mtx:patent&rft.genre=patent&rft.au=QI%20XIANGYU&rft.date=2023-10-13&rft_id=info:doi/&rft_dat=%3Cepo_EVB%3ECN116875903A%3C/epo_EVB%3E%3Curl%3E%3C/url%3E&disable_directlink=true&sfx.directlink=off&sfx.report_link=0&rft_id=info:oai/&rft_id=info:pmid/&rfr_iscdi=true |