Amorphous and nanocrystalline magnetic core processing technology

The invention discloses an amorphous and nanocrystalline magnetic core processing technology. The amorphous and nanocrystalline magnetic core processing technology comprises the following steps that S1, a magnetic core is placed in sizing glue to be soaked; step S2, baking the soaked magnetic core; s3, the magnetic core is placed in a container containing curing glue to be soaked, and the curing glue completely submerges the magnetic core; s4, the container and the magnetic core in the container are jointly placed in a vacuumizer, and after overflowing bubbles of the magnetic core in the vacuum environment are not obvious, the magnetic core continues to stand; s5, the magnetic core is placed in an oven to be baked, firstly, the baking temperature is controlled within the range of 100 +/-5 DEG C, heat preservation is conducted for 180 minutes, and then the baking temperature is adjusted within the range of 170 +/-5 DEG C, and heat preservation is conducted for 240 minutes; and S6, the baked magnetic core is ta