Manufacturing method of pattern ice skate blade material

The invention discloses a manufacturing method of a patterned ice skate blade material and belongs to the field of metal materials. According to the invention, a vacuum gas atomization powder preparation technology is adopted to prepare the high-temperature-resistant and high-pressure-resistant ceramic powder, 1.8%-2.2% of Si; 1.8% to 2.2% of Mn; 4.8% to 5.2% of Mo; 4.8% to 5.2% of W; 3.8 to 4.2 percent of Cr; 1.8% to 2.2% of Nb; 0.8% to 1.2% of Ta; 2.8% to 3.2% of Ti; 2.8% to 3.2% of V; 1.8% to 2.2% of B; the preparation method comprises the following steps: preparing spherical powder from the following components in percentage by weight: 3.8-4.2% of Al and the balance of Fe, the particle size of the powder is in a range of 5-150 microns, the densification temperature of the powder subjected to hot isostatic pressing sintering is 1190-1210 DEG C, forging and rolling a sintered hot isostatic pressing ingot into a plate, the forging and hot rolling temperature is 980-1180 DEG C, the thickness of a hot-rolled p