Composicion cementicia, que contiene una fase continua que resulta del curado de una mezcla cementicia, en ausencia de harina de silice, y que comprende cemento inorganico, mineral inorganico, relleno puzolanico, policarboxilato y agua; y uso de la composicion en una panel y barrera cementicia

LA INVENCIÓN SE REFIERE A UNA COMPOSICIÓN CEMENTICIA DIMENSIONALMENTE ESTABLE, QUE COMPRENDE: UNA FASE CONTINUA QUE RESULTA DEL CURADO DE UNA MEZCLA CEMENTICIA ACUOSA AUTONIVELANTE, EN AUSENCIA DE HARINA DE SÍLICE DE 25-45% EN PESO DE CARPETA DE CEMENTO INORGÁNICO; 35-65% EN PESO DE RELLENO MINERAL INORGÁNICO QUE TIENE UN TAMAÑO DE PARTICULA DE ALREDEDOR DE 150-450 MICRONES; 5-15% EN PESO DE RELLENO PUZOLÁNICO QUE TIENE UN TAMAÑO DE PARTÍCULA MEDIO MENOR QUE O IGUAL QUE 50 MICRONES; 0,25-5,0% EN PESO DE AGENTE AUTONIVELANTE BASADO EN POLICARBOXILATO; Y 612% EN PESO DE AGUA. ADICIONALMENTE, SE REIVINDICA EL USO DE DICHA COMPOSICIÓN QUE SIRVE PARA UN PANEL CEMENTICIO BLINDADO Y UNA BARRERA CEMENTICIA. A self-leveling cementitious mixture with excellent flow properties and which hardens with a controlled rate of strength development to an ultra-high compressive strength composite composition for use in making articles such as cementitious armor panel with ballistic and blast resistant properties including: a continuous phase resulting from the curing of an aqueous mixture, in the absence of silica flour, of inorganic cement binder, inorganic mineral filler having a particle size of about 150-450 microns, pozzolanic mineral filler, polycarboxylate based self-leveling agent and water. The cementitious mixture may include alkanolamine, such as triethanolamine, and acid or acid salt, such as tartaric acid. The cementitious composition may be reinforced with reinforcing fibers, e.g. glass fibers, in an amount of about 0.5-6.0% by volume of the overall cementitious composition. The fibers are uniformly dispersed in the cementitious composition before it is cured to form a final cementitious armor panel.