Study the effect of gamma radiation on the some properties of glass and glass-ceramic immobilize nuclear waste

Vitrifications process one of the important methods to immobilize nuclear waste. In this research nuclear waste (Strontium Oxides) with molecular weight (5 %) was immobilized by vitrification methods in two types of borosilicate glass (c-type) which are glass and glass-ceramics. To investigate the physical, chemical and mechanical properties of glass and glass-ceramic after immobilize nuclear waste these samples irradiated by gamma ray radiation. Co-60 was used as gamma a irradiation with dose rate 0.38 kGy / hr for different period of time. It’s found that gamma radiation affected the glass and glass-ceramic properties. From phase analysis by the x-ray diffraction for glass-ceramic samples proved that at doses 343kGy change the crystalline glass to amorphous glass. A conclusion from these ionization studies is that the limited magnitude of Strontium ion leaching associated with ionization damage does not appear to pose any direct problems for the safe storage of nuclear waste glass. إن عملية معالجة النفايات المشعة بواسطة تثبيتها في الزجاج واحدة من الطرق المهمة لمنع حركة النفايات النووية. في هذا البحث استعمل أوكسيد السنترنتيوم بنسبة وزنية 5 % كنفايات مشعة, زجج في نوعين من الزجاج : البورسليكات (نوع C) الزجاج و الزجاج – السيراميك. و تم دراسة الخواص الفيزيائية و الكيميائية للزجاج و الزجاج-السيراميك بعد تزجيج النفايات النووية المشعة بواسطة تشعيعها بأشعة كاما. تم استخدام الكوبلت 60-كنظير باعث لأشعة كاما بمعدل جرعة 0.38 كيلو كراي / ساعة لفترات مختلفة من الزمن. وجد أن أشعة كاما أثرت على خواص الزجاج و الزجاج-السيراميك, و عند الجرعة الإشعاعية 343 كيلو كراي تحول الزجاج-السيراميك من الطور البلوري إلى زجاج عشوائي. و من نتائج هذه الدراسة تبين أن نضوح أيون السترونتيوم بعد التعرض لأشعة كاما يكون قليل جدا بحيث لا يشكل خطر, لذلك فإن خزن النفايات المشعة في الزجاج تكون طريقة جيدة.