Water absorption and mechanical properties of high-density polyethylene / egg shell composite

I n this research, the water absorption and mechanical properties of (high-density polyethylene egg shell) composites as a function of egg shell powder weight content in the grain size (75,125 μm) were investigated. Polymer composite was fabricated by mixing (HDPE) with (5, 10, 15, 20, 25) wt. % of egg shell powder to obtain desirable properties. The parameters such as tensile strength, tensile modulus, elongation at break and impact test were carried out on the prepared samples. It was found that the addition of egg shell powder to the polymer leads to decrease the tensile strength, modulus of elasticity, shore-D hardness on other hand it increases the % elongation at break, and for the impact strength. Water absorption of the composites behaviors as function of days has also been investigated, and it increases by increasing exposure time for the same filler content, while the absorbed amount of water increases, by increasing the wt. % of egg shell constant exposure time. تم في هذا البحث دراسة الخواص الميكانيكية و امتصاصية الماء للبولي أثيلين عالي الكثافة كدالة للنسبة الوزنية لقشور البيض عند الحجم دقائقي (75,125 um). تم تحضير المتراكبات بمزج البوليمر مع نسب وزنية مختلفة (5%, 10 %, 15 %, 20 %, 25 %) من قشور البيض للحصول على أفضل الخصائص. تمت دراسة السلوك الميكانيكي لهذا الخليط من خلال دراسة الفحوصات الاتلافية (فحص الشد و معامل المرونة و الاستطالة عند الكسر و فحص الصدم). أظهرت النتائج العملية بأن إضافة قشور البيض تعمل على تقليل قوة الإجهاد و معامل يونك و الإجهاد عند الوهن. كما وجد أن مقدار الاستطالة عند الكسر و فحص الصدم يقل بزيادة تركيز المضاف. كما تم دراسة سلوك امتصاصية الماء كدالة للزمن للمتراكبات المحضرة. و تبين بأن كمية الماء الممتصة تزداد بزيادة فترة التعرض إلى الماء عند ثبوت نسبة قشور البيض، كما إنها (تزداد، تقل) بازدياد نسبة قشور البيض عند ثبوت زمن التعرض.