Experimental investigation of the viscoplastic behaviours and microstructure evolutions of AZ31B and Elektron 717 Mg-alloys
An insight into the thermo-mechanical behaviours of AZ31B and Elektron 717 magnesium alloys under the hot stamping conditions was established. High-temperature tensile tests (i.e. 350–450 °C) at a strain rate of 0.1 to 5/s were conducted to examine the material viscoplastic behaviours. Additionally,...
Gespeichert in:
Veröffentlicht in: | Materials & design 2019-12, Vol.184, p.108160, Article 108160 |
---|---|
Hauptverfasser: | , , , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | An insight into the thermo-mechanical behaviours of AZ31B and Elektron 717 magnesium alloys under the hot stamping conditions was established. High-temperature tensile tests (i.e. 350–450 °C) at a strain rate of 0.1 to 5/s were conducted to examine the material viscoplastic behaviours. Additionally, microstructure characterizations were performed, using the electron backscatter diffraction (EBSD), on the deformed samples to capture the underlying deformation mechanisms. Dynamic recrystallization (DRX) and texture formation were observed during the deformation at high temperature in both alloys and are the primary factors that affect the viscoplastic behaviours. The yield stress of both alloys reduced with increasing temperatures and reducing strain rates. More importantly, the ductility of the samples increased with both the temperatures and the strain rates. The higher ductility at higher strain rates was primarily attributed to finer grains and the slightly weakened textures, enabling a more uniform deformation. A maximum ductility of ~2 was observed in AZ31B under 450 °C at 1/s while ~0.9 in Elektron 717 under the identical condition. The addition of rare earth elements in Elektron 717 may suppress the active DRX. The recrystallization type was identified as discontinuous DRX. The research findings deliver understandings on the viscoplastic behaviours and the deformation mechanisms of AZ31B and Elektron 717 under the hot stamping conditions and provide scientific guidance for feasibility study on applying hot stamping technique to Mg-alloy for forming complex geometry components.
[Display omitted]
•Viscoplastic behaviours of AZ31B and Elektron717 alloys under hot stamping conditions were studied.•The ductility of AZ31B and Elektron717 increased with strain rates and temperatures.•Rare earth elements in Elektron717 suppressed the recrystallization and grain growth.•Analyses of the grain size, texture and geometrically necessary dislocations in the hot deformation were performed. |
---|---|
ISSN: | 0264-1275 1873-4197 |
DOI: | 10.1016/j.matdes.2019.108160 |