Titan Yellow and Congo Red Removal with Superparamagnetic Iron-Oxide-Based Nanoparticles Doped with Zinc

In this work, we present magnetic nanoparticles based on iron oxide doped with zinc synthesized using the wet co-precipitation method for environmental application. The morphology of the samples was revealed by SEM and TEM, which showed particles of granular shape and size of about 15 nm. The specific surface areas of the materials using the BET method were within the range of 85.7 to 101.5 m2 g−1 depending on the zinc content in the superparamagnetic iron oxide nanoparticles (SPIONs). Magnetometry was performed to determine the magnetic properties of the particles, indicating superparamagnetism. Synthesized magnetic nanoparticles with different amounts of zinc dopant were used as an adsorbent to remove model pollutant Titan yellow (TY) from the aqueous solutions. Adsorption was determined by investigating the effects of sorbent amount, dye concentration, and contact time. The synthesized material removed Titan yellow quickly and efficiently within the physical adsorption. The adsorption isotherms were consistent with the models proposed by Langmuir and Redlich-Peterson. The monolayer adsorption capacities were 30 and 43 mg g−1 for Fe3O4 and Fe3O4@10%Zn, respectively, for the removal of TY. However, that of Congo red is 59 mg g−1 by Fe3O4@10%Zn. The proposed nanoparticles offer fast and cost-effective water purification, and they can be separated from solution using magnets.