Milling of TiBbm 2 Particle Reinforced High-Modulus Steel
TiB 2 particle reinforced high-stiffness steel is one of the composite materials that aim to improve Young’s modulus by compositing TiB 2 particles into a stainless steel base phase. This material is designed to exhibit higher rigidity and strength than conventional iron-based materials by using TiB...
Gespeichert in:
Veröffentlicht in: | International journal of automation technology 2024-05, Vol.18 (3), p.358-365 |
---|---|
Hauptverfasser: | , , , , |
Format: | Artikel |
Sprache: | eng |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | TiB
2
particle reinforced high-stiffness steel is one of the composite materials that aim to improve Young’s modulus by compositing TiB
2
particles into a stainless steel base phase. This material is designed to exhibit higher rigidity and strength than conventional iron-based materials by using TiB
2
particles as the reinforcing phase, and is expected to reduce the weight of high-load components in engines. For this reason, tool life is very short when machining this material. Therefore, high Young’s modulus steel containing TiB
2
particles is known to be one of the most difficult-to-cut materials. The purpose of this study was to investigate how to extend tool life in the milling of high-Young’s-modulus steel. Cutting speed dependence of tool life was investigated by end milling using a binderless CBN tool with excellent hardness and bending strength. In addition, the tool damage mechanism was also investigated. The results showed that tools composed of binderless CBN tool have a longer life than conventional CBN tool. In this type of binderless CBN tool, the tool wear rate tended to increase with increasing cutting speed. In addition, the longest tool life was obtained at a cutting speed of 1.25 m/s, though wear rate increased at a boundary cutting length of 1300 m. The wear rate was found to increase with increasing cutting speed. Temperature measurement results indicate that the primary cause of tool damage was mechanical wear, as the temperatures were much too low for a reaction between cBN and Fe. Friction tests revealed scratch marks on the tool originating from crushed cBN particles produced by the crushing of the cutting edge. This indicates that wear is accelerated by the high frictional energy of the cBN powder rubbing against the flank face. |
---|---|