In situ forming asymmetric bi-functional gel polymer electrolyte in lithium-sulfur batteries

An asymmetric bi-functional gel polymer electrolyte (GPE) with an interpenetrating network (IPN) has been prepared by in situ cationic polymerization of 1,3-dioxolane (DOL) (PDXL) and cross-linking of cyanoethyl polyvinyl alcohol (PVA-CN), which is initiated by lithium hexafluorophosphate. The mechanism of the Ritter reaction was proposed for the cross-linking of PVA-CN. The IPN-GPE has a high ionic conductivity (3.23 x 10(-3) S cm(-1) at 25 degrees C) and high t(Li)(+) (0.81). Li-S batteries with the asymmetric GPE exhibit good cycle stability (807 mA h g(-1) after 500 cycles at 0.5C) and high Coulombic efficiency (similar to 99.6%). Furthermore, the self-discharge of Li-S batteries can be greatly inhibited, and only 6.4% of capacity loss is observed after 24 hours. The improved performance can be ascribed to the bi-functional GPE, i.e. immobilizing soluble Li polysulfides by the carbonyl groups of the IPN-GPE in the cathode side and promoting uniform Li deposition by the PDXL-GPE in the anode side. Our work has provided a meaningful strategy for in situ forming bi-functional GPEs to improve the performance of Li-S batteries.