Liquid metal embrittlement (LME) is one of the least studied forms of environmental fracture. The phenomenon has been recognised for over a century, but although industrially important, it has not received the same attention as other forms of environmental cracking such as stress corrosion cracking...

Ausführliche Beschreibung

Bibliographische Detailangaben

Veröffentlicht in:	Materials Science 1992-09, Vol.27 (5), p.453-459
Hauptverfasser:	Clegg, R. E., Jones, D. R. H.
Format:	Artikel
Sprache:	eng
Schlagworte:	ALLOYS CORROSION CRACK PROPAGATION CRACKS EMBRITTLEMENT FAILURES MATERIALS SCIENCE STRESS CORROSION