Conditioning of austenite by hot working of microalloyed forging steels

On four grades of medium carbon V‐bearing steels with additional Ti and Nb microalloying hot deformation tests were conducted as a simulation of hot forging. The aim of the study was to suggest general guidelines for the design of deformation patterns and cooling conditions of austenite. Both the resulting flow stresses and the strengthening/softening behaviour were taken into consideration. The maximum flow stresses appear to be insensitive both to the variation of microalloying and to the design of the deformation schedule over the range tested. Nevertheless, large differences can be achieved regarding austenite strengthening, especially its residual value at the begin of the γ‐α‐transformation which is decisive for the subsequent transformation process. A substantial effect of the final deformation temperature and the type of microalloying was ascertained. An vier V‐haltigen Stählen mit mittlerem Kohlenstoffgehalt und zusätzlicher Mikrolegierung mit Ti und Nb wurden Warmumformversuche zur Simulation des Warmschmiedens durchgeführt mit dem Ziel, allgemeine Richtlinien für die Gestaltung der Umformsequenzen und der Temperaturführung im Austenit zu erörtern. Dabei wurden vor allem die resultierenden Fließspannungen und das Ver‐ und Entfestigungsverhalten des Austenits berücksichtigt. Im untersuchten Parameterbereich zeigen die maximalen Fließspannungen eine weitgehende Unempfindlichkeit sowohl auf die Variation der Mikrolegierung als auch auf die Gestaltung der Umformsequenzen. Dementgegen konnten signifikante Unterschiede bezüglich der Austenitverfestigung ermittelt werden, besonders in der Höhe der im Austenit zu Beginn der γ‐α‐Umwandlung verbliebenen und für den Ablauf des nachfolgenden Umwandlungsprozesses entscheidenden Restverfestigung. Es wurde ein erheblicher Einfluß der Endumformtemperatur sowie der Art von Mikrolegierung auf die Restverfestigung festgestellt.