Fatigue crack growth in mooring chain steel at different mean load levels
The fatigue crack growth rates of R4 mooring chain steel at different R-ratios are investigated. Crack growth experiments are performed at three different R-ratios, 0.1, 0.3 and 0.7, utilizing compact tension specimens in air environment. Huang and Moan’s driving force parameter ΔKE, which relates t...