Suppression of Photoinduced BBO Defects Generation on TIO2（110） by Water

We have investigated creation of variable concentrations of defects on TIO2（110）-（1×1） surface by 266 nm laser using temperature programmed desorption technique. Oxygen-vacancy defects can be easily induced by ultraviolet light, the defects concentration has a linear dependence on power density higher than 50 mW/cm2 for 90 s irradiation. No observation of O2 molecule and Ti atom desorption suggests that UV induced defects creation on TiO2（110）-（1×1） is an effective and gentle method. With pre-dosage of thin films of water, the rate of defects creation on TiO2（110）-（1×1） is slower at least by two orders of magnitude than bare TiO2（110）-（1×1） surface. Further investigations show that water can be more easily desorbed by UV light, and thus desorption of bridging oxygen is depressed.