Hydrothermal formation of dispersive Mg(OH)2 particles in NaOH solution

The hydrothermal modification of Mg(OH)2 crystals in NaOH solution was investigated. The aggregated Mg(OH)2 particles with irregular shape are converted to regular Mg(OH)2 hexagonal plates after hydrothermal treatment. The prolongation of reaction time from 1-4 h or the increase of temperature from...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Transactions of Nonferrous Metals Society of China 2004, Vol.14 (2), p.370-375
1. Verfasser: 向兰 金永成 金涌
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The hydrothermal modification of Mg(OH)2 crystals in NaOH solution was investigated. The aggregated Mg(OH)2 particles with irregular shape are converted to regular Mg(OH)2 hexagonal plates after hydrothermal treatment. The prolongation of reaction time from 1-4 h or the increase of temperature from 140℃ to 200℃ can promote the formation of Mg(OH)2 plates with big particle size but small cluster size. The dispersion characteristics of the hydrothermal products are improved owing to the improvement of Mg(OH)2 crystalline degree and the in-crease of I(001)/I(101) ratio. The proper hydrothermal modification condition is as follows: solid content 0. 075 g/mL,NaOH concentration 5.0 mol/L, temperature 200℃ and time 4 h. Thermodynamic analysis indicates that the increase of MgOH^+ concentration at elevated temperature or the increase of OH^- concentration in concentrated NaOH solution is favorable for the hydrothermal formation of Mg(OH)2 particles.
ISSN:1003-6326