Dielectric and piezoelectric properties of （Li, Ce） modified NaBi5Ti5O18 composite ceramics

Nominal （Li0.5Ce0.5）x（Na0.5Bi0.5）（1-x）Na0.5Bi4.5Ti5O18 composite ceramics were fabricated using conventional solid-state reaction method. The coexistence of bismuth layer-structured phase and perovskite phase was determined in these ceramics using XRD technique. At room temperature, the x=0.11 sample showed the largest piezoelectric constant, d33, of about 26.5 pC/N and the largest electromechanical coupling factor, kt, of about 30%. Even after annealing at 500 ℃, the value of d33 was still about 19 pC/N, in x=0.08-0.11 samples. Moreover these composite ceramics showed low temperature coefficients of dielectric constant and high electrical resistivity in the temperature region of 450-550 ℃. These results indicated that （Li, Ce） modified NaBi5Ti5O18 composite ceramics were promising piezoelectric materials for high-temperature applications.