Effect of Heat Treatment on the Lithium Ion Conduction of the LiBH4–LiI Solid Solution

The LiBH4–LiI solid solution is a good Li+ conductor and a promising crystalline electrolyte for all-solid-state lithium based batteries. The focus of the present work is on the effect of heat treatment on the Li+ conduction. Solid solutions with a LiI content of 6.25–50% were synthesized by high-en...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of physical chemistry. C 2013-02, Vol.117 (7), p.3249-3257
Hauptverfasser: Sveinbjörnsson, Dadi, Myrdal, Jon Steinar Gardarsson, Blanchard, Didier, Bentzen, Janet Jonna, Hirata, Takumi, Mogensen, Mogens Bjerg, Norby, Poul, Orimo, Shin-Ichi, Vegge, Tejs
Format: Artikel
Sprache:eng ; jpn
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
container_end_page 3257
container_issue 7
container_start_page 3249
container_title Journal of physical chemistry. C
container_volume 117
creator Sveinbjörnsson, Dadi
Myrdal, Jon Steinar Gardarsson
Blanchard, Didier
Bentzen, Janet Jonna
Hirata, Takumi
Mogensen, Mogens Bjerg
Norby, Poul
Orimo, Shin-Ichi
Vegge, Tejs
description The LiBH4–LiI solid solution is a good Li+ conductor and a promising crystalline electrolyte for all-solid-state lithium based batteries. The focus of the present work is on the effect of heat treatment on the Li+ conduction. Solid solutions with a LiI content of 6.25–50% were synthesized by high-energy ball milling and annealed at 140 °C. Powder X-ray diffraction and scanning electron microscopy were used for characterizing the samples and for comparing their crystallite sizes and the density of defects before and after the annealing. The Li+ conductivity was measured using impedance spectroscopy, resulting in conductivities exceeding 0.1 mS/cm at 30 °C and 10 mS/cm at 140 °C. It was found that the formation of defect-rich microstructures during ball milling increased the specific conductivities of these compounds significantly. The phase transition temperatures between the orthorhombic and hexagonal structures of LiBH4 were measured using differential scanning calorimetry (DSC). The measured transition temperatures range from 100 to −70 °C and show a linear decrease of 70 °C for every 10% of LiI addition up to a LiI content of 25%. The relative stability of the two structures was calculated using density functional theory, and together with the DSC measurements, the calculations were used to evaluate the change in entropic difference between the structures with LiI content.
doi_str_mv 10.1021/jp310050g
format Article
fullrecord <record><control><sourceid>acs</sourceid><recordid>TN_cdi_acs_journals_10_1021_jp310050g</recordid><sourceformat>XML</sourceformat><sourcesystem>PC</sourcesystem><sourcerecordid>b352650879</sourcerecordid><originalsourceid>FETCH-LOGICAL-a966-5ed2f6dafd6b8118aae3a94fbdbd8ba6c6731c9031e900ea245ae452c0f9fd353</originalsourceid><addsrcrecordid>eNo9kD1Ow0AQhVcIJEKg4AbbUBp2vD_2lmCF2JIlClzQWeP9IbYSG8V2zx24ISdhraA0b97MfJqRHiH3wB6BxfDUfXFgTLLPC7ICzeMoEVJenr1IrsnNOHYB4Qz4inxsvHdmooOnucOJVsegB9eHSU-nnaNlO-3a-UCL0GdDb2cztcEG_rR9ycXv90_ZFvR92Ld20XkhbsmVx_3o7v7rmlSvmyrLo_JtW2TPZYRaqUg6G3tl0VvVpAApouOohW9sY9MGlVEJB6MZB6cZcxgLiU7I2DCvveWSr8nD6Syase6G-diHZzWwekmjPqfB_wBmHFLZ</addsrcrecordid><sourcetype>Publisher</sourcetype><iscdi>true</iscdi><recordtype>article</recordtype></control><display><type>article</type><title>Effect of Heat Treatment on the Lithium Ion Conduction of the LiBH4–LiI Solid Solution</title><source>ACS Publications</source><creator>Sveinbjörnsson, Dadi ; Myrdal, Jon Steinar Gardarsson ; Blanchard, Didier ; Bentzen, Janet Jonna ; Hirata, Takumi ; Mogensen, Mogens Bjerg ; Norby, Poul ; Orimo, Shin-Ichi ; Vegge, Tejs</creator><creatorcontrib>Sveinbjörnsson, Dadi ; Myrdal, Jon Steinar Gardarsson ; Blanchard, Didier ; Bentzen, Janet Jonna ; Hirata, Takumi ; Mogensen, Mogens Bjerg ; Norby, Poul ; Orimo, Shin-Ichi ; Vegge, Tejs</creatorcontrib><description>The LiBH4–LiI solid solution is a good Li+ conductor and a promising crystalline electrolyte for all-solid-state lithium based batteries. The focus of the present work is on the effect of heat treatment on the Li+ conduction. Solid solutions with a LiI content of 6.25–50% were synthesized by high-energy ball milling and annealed at 140 °C. Powder X-ray diffraction and scanning electron microscopy were used for characterizing the samples and for comparing their crystallite sizes and the density of defects before and after the annealing. The Li+ conductivity was measured using impedance spectroscopy, resulting in conductivities exceeding 0.1 mS/cm at 30 °C and 10 mS/cm at 140 °C. It was found that the formation of defect-rich microstructures during ball milling increased the specific conductivities of these compounds significantly. The phase transition temperatures between the orthorhombic and hexagonal structures of LiBH4 were measured using differential scanning calorimetry (DSC). The measured transition temperatures range from 100 to −70 °C and show a linear decrease of 70 °C for every 10% of LiI addition up to a LiI content of 25%. The relative stability of the two structures was calculated using density functional theory, and together with the DSC measurements, the calculations were used to evaluate the change in entropic difference between the structures with LiI content.</description><identifier>ISSN: 1932-7447</identifier><identifier>EISSN: 1932-7455</identifier><identifier>DOI: 10.1021/jp310050g</identifier><language>eng ; jpn</language><publisher>American Chemical Society</publisher><ispartof>Journal of physical chemistry. C, 2013-02, Vol.117 (7), p.3249-3257</ispartof><rights>Copyright © 2013 American Chemical Society</rights><woscitedreferencessubscribed>false</woscitedreferencessubscribed></display><links><openurl>$$Topenurl_article</openurl><openurlfulltext>$$Topenurlfull_article</openurlfulltext><thumbnail>$$Tsyndetics_thumb_exl</thumbnail><linktopdf>$$Uhttps://pubs.acs.org/doi/pdf/10.1021/jp310050g$$EPDF$$P50$$Gacs$$H</linktopdf><linktohtml>$$Uhttps://pubs.acs.org/doi/10.1021/jp310050g$$EHTML$$P50$$Gacs$$H</linktohtml><link.rule.ids>314,780,784,27076,27924,27925,56738,56788</link.rule.ids></links><search><creatorcontrib>Sveinbjörnsson, Dadi</creatorcontrib><creatorcontrib>Myrdal, Jon Steinar Gardarsson</creatorcontrib><creatorcontrib>Blanchard, Didier</creatorcontrib><creatorcontrib>Bentzen, Janet Jonna</creatorcontrib><creatorcontrib>Hirata, Takumi</creatorcontrib><creatorcontrib>Mogensen, Mogens Bjerg</creatorcontrib><creatorcontrib>Norby, Poul</creatorcontrib><creatorcontrib>Orimo, Shin-Ichi</creatorcontrib><creatorcontrib>Vegge, Tejs</creatorcontrib><title>Effect of Heat Treatment on the Lithium Ion Conduction of the LiBH4–LiI Solid Solution</title><title>Journal of physical chemistry. C</title><addtitle>J. Phys. Chem. C</addtitle><description>The LiBH4–LiI solid solution is a good Li+ conductor and a promising crystalline electrolyte for all-solid-state lithium based batteries. The focus of the present work is on the effect of heat treatment on the Li+ conduction. Solid solutions with a LiI content of 6.25–50% were synthesized by high-energy ball milling and annealed at 140 °C. Powder X-ray diffraction and scanning electron microscopy were used for characterizing the samples and for comparing their crystallite sizes and the density of defects before and after the annealing. The Li+ conductivity was measured using impedance spectroscopy, resulting in conductivities exceeding 0.1 mS/cm at 30 °C and 10 mS/cm at 140 °C. It was found that the formation of defect-rich microstructures during ball milling increased the specific conductivities of these compounds significantly. The phase transition temperatures between the orthorhombic and hexagonal structures of LiBH4 were measured using differential scanning calorimetry (DSC). The measured transition temperatures range from 100 to −70 °C and show a linear decrease of 70 °C for every 10% of LiI addition up to a LiI content of 25%. The relative stability of the two structures was calculated using density functional theory, and together with the DSC measurements, the calculations were used to evaluate the change in entropic difference between the structures with LiI content.</description><issn>1932-7447</issn><issn>1932-7455</issn><fulltext>true</fulltext><rsrctype>article</rsrctype><creationdate>2013</creationdate><recordtype>article</recordtype><sourceid/><recordid>eNo9kD1Ow0AQhVcIJEKg4AbbUBp2vD_2lmCF2JIlClzQWeP9IbYSG8V2zx24ISdhraA0b97MfJqRHiH3wB6BxfDUfXFgTLLPC7ICzeMoEVJenr1IrsnNOHYB4Qz4inxsvHdmooOnucOJVsegB9eHSU-nnaNlO-3a-UCL0GdDb2cztcEG_rR9ycXv90_ZFvR92Ld20XkhbsmVx_3o7v7rmlSvmyrLo_JtW2TPZYRaqUg6G3tl0VvVpAApouOohW9sY9MGlVEJB6MZB6cZcxgLiU7I2DCvveWSr8nD6Syase6G-diHZzWwekmjPqfB_wBmHFLZ</recordid><startdate>20130221</startdate><enddate>20130221</enddate><creator>Sveinbjörnsson, Dadi</creator><creator>Myrdal, Jon Steinar Gardarsson</creator><creator>Blanchard, Didier</creator><creator>Bentzen, Janet Jonna</creator><creator>Hirata, Takumi</creator><creator>Mogensen, Mogens Bjerg</creator><creator>Norby, Poul</creator><creator>Orimo, Shin-Ichi</creator><creator>Vegge, Tejs</creator><general>American Chemical Society</general><scope/></search><sort><creationdate>20130221</creationdate><title>Effect of Heat Treatment on the Lithium Ion Conduction of the LiBH4–LiI Solid Solution</title><author>Sveinbjörnsson, Dadi ; Myrdal, Jon Steinar Gardarsson ; Blanchard, Didier ; Bentzen, Janet Jonna ; Hirata, Takumi ; Mogensen, Mogens Bjerg ; Norby, Poul ; Orimo, Shin-Ichi ; Vegge, Tejs</author></sort><facets><frbrtype>5</frbrtype><frbrgroupid>cdi_FETCH-LOGICAL-a966-5ed2f6dafd6b8118aae3a94fbdbd8ba6c6731c9031e900ea245ae452c0f9fd353</frbrgroupid><rsrctype>articles</rsrctype><prefilter>articles</prefilter><language>eng ; jpn</language><creationdate>2013</creationdate><toplevel>online_resources</toplevel><creatorcontrib>Sveinbjörnsson, Dadi</creatorcontrib><creatorcontrib>Myrdal, Jon Steinar Gardarsson</creatorcontrib><creatorcontrib>Blanchard, Didier</creatorcontrib><creatorcontrib>Bentzen, Janet Jonna</creatorcontrib><creatorcontrib>Hirata, Takumi</creatorcontrib><creatorcontrib>Mogensen, Mogens Bjerg</creatorcontrib><creatorcontrib>Norby, Poul</creatorcontrib><creatorcontrib>Orimo, Shin-Ichi</creatorcontrib><creatorcontrib>Vegge, Tejs</creatorcontrib><jtitle>Journal of physical chemistry. C</jtitle></facets><delivery><delcategory>Remote Search Resource</delcategory><fulltext>fulltext</fulltext></delivery><addata><au>Sveinbjörnsson, Dadi</au><au>Myrdal, Jon Steinar Gardarsson</au><au>Blanchard, Didier</au><au>Bentzen, Janet Jonna</au><au>Hirata, Takumi</au><au>Mogensen, Mogens Bjerg</au><au>Norby, Poul</au><au>Orimo, Shin-Ichi</au><au>Vegge, Tejs</au><format>journal</format><genre>article</genre><ristype>JOUR</ristype><atitle>Effect of Heat Treatment on the Lithium Ion Conduction of the LiBH4–LiI Solid Solution</atitle><jtitle>Journal of physical chemistry. C</jtitle><addtitle>J. Phys. Chem. C</addtitle><date>2013-02-21</date><risdate>2013</risdate><volume>117</volume><issue>7</issue><spage>3249</spage><epage>3257</epage><pages>3249-3257</pages><issn>1932-7447</issn><eissn>1932-7455</eissn><abstract>The LiBH4–LiI solid solution is a good Li+ conductor and a promising crystalline electrolyte for all-solid-state lithium based batteries. The focus of the present work is on the effect of heat treatment on the Li+ conduction. Solid solutions with a LiI content of 6.25–50% were synthesized by high-energy ball milling and annealed at 140 °C. Powder X-ray diffraction and scanning electron microscopy were used for characterizing the samples and for comparing their crystallite sizes and the density of defects before and after the annealing. The Li+ conductivity was measured using impedance spectroscopy, resulting in conductivities exceeding 0.1 mS/cm at 30 °C and 10 mS/cm at 140 °C. It was found that the formation of defect-rich microstructures during ball milling increased the specific conductivities of these compounds significantly. The phase transition temperatures between the orthorhombic and hexagonal structures of LiBH4 were measured using differential scanning calorimetry (DSC). The measured transition temperatures range from 100 to −70 °C and show a linear decrease of 70 °C for every 10% of LiI addition up to a LiI content of 25%. The relative stability of the two structures was calculated using density functional theory, and together with the DSC measurements, the calculations were used to evaluate the change in entropic difference between the structures with LiI content.</abstract><pub>American Chemical Society</pub><doi>10.1021/jp310050g</doi><tpages>9</tpages></addata></record>
fulltext fulltext
identifier ISSN: 1932-7447
ispartof Journal of physical chemistry. C, 2013-02, Vol.117 (7), p.3249-3257
issn 1932-7447
1932-7455
language eng ; jpn
recordid cdi_acs_journals_10_1021_jp310050g
source ACS Publications
title Effect of Heat Treatment on the Lithium Ion Conduction of the LiBH4–LiI Solid Solution
url https://sfx.bib-bvb.de/sfx_tum?ctx_ver=Z39.88-2004&ctx_enc=info:ofi/enc:UTF-8&ctx_tim=2025-01-04T18%3A05%3A06IST&url_ver=Z39.88-2004&url_ctx_fmt=infofi/fmt:kev:mtx:ctx&rfr_id=info:sid/primo.exlibrisgroup.com:primo3-Article-acs&rft_val_fmt=info:ofi/fmt:kev:mtx:journal&rft.genre=article&rft.atitle=Effect%20of%20Heat%20Treatment%20on%20the%20Lithium%20Ion%20Conduction%20of%20the%20LiBH4%E2%80%93LiI%20Solid%20Solution&rft.jtitle=Journal%20of%20physical%20chemistry.%20C&rft.au=Sveinbjo%CC%88rnsson,%20Dadi&rft.date=2013-02-21&rft.volume=117&rft.issue=7&rft.spage=3249&rft.epage=3257&rft.pages=3249-3257&rft.issn=1932-7447&rft.eissn=1932-7455&rft_id=info:doi/10.1021/jp310050g&rft_dat=%3Cacs%3Eb352650879%3C/acs%3E%3Curl%3E%3C/url%3E&disable_directlink=true&sfx.directlink=off&sfx.report_link=0&rft_id=info:oai/&rft_id=info:pmid/&rfr_iscdi=true